LNP™ THERMOCOMP™ Compound ZFM3314
SABIC's Specialties Business LNP™ THERMOCOMP™ ZFM3314 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing 20% glass fiber. Added features of this grade include: Non-Brominated & Non-Chlorinated Flame Retardant, Impact Modified, Heat Stabilized.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Density
- 1250.0 - 1250.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 5800.0 - 5800.0 MPa
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Fillers Included
- Glass Fiber
- Mica
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Impact Modifier
- Material Features
- Cost Effective
- Flame Retardant
- Heat Stabilized
- High Impact Resistance
- High Stiffness
- Impact Modified
- Low Warpage
- Non-brominated
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 95 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.1 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 6100 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 145 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 5800 | MPa | ISO 178 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 300°C, 5.0 kg) ¹¹ | 17 | cm³/10 min | ISO 1133 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000032 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000062 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 179 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 170 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
Table 5 of 5
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 2 - 8 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 295 - 315 | °C |
| Nozzle Temperature ⁷ | 295 - 315 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 315 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 310 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 305 | °C |
| Mold Temperature ⁷ | 75 - 105 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |