LNP™ THERMOCOMP™ Compound UF009S

Chemical Family: Polyamides

SABIC's Specialties Business LNP THERMOCOMP UF009S compound is based on Polyphthalamide (PPA) resin containing 45% glass fiber. Added features of this grade include: Heat Stabilized. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Semiconductor Manufacturing
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyphthalamide (PPA)
Fillers Included: Glass Fiber
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Cost Effective
Heat Stabilized
High Stiffness
High Temperature Resistance
No Added PFAS
Very Good Heat Resistance
Country Availability: Brazil
Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Under The Hood
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	253	MPa	ISO 527
Tensile Stress (Break) ¹¹	242	MPa	ASTM D638
Tensile Strain (Break) ¹¹	1.7	%	ASTM D638
Tensile Strain (Break) ¹¹	1.8	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	20350	MPa	ASTM D638
Flexural Stress ¹¹	392	MPa	ASTM D790
Flexural Stress ¹¹	386	MPa	ISO 178
Flexural Modulus ¹¹	18760	MPa	ASTM D790
Flexural Modulus ¹¹	18330	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	22740	MPa	ISO 527

Table 2 of 5

8 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.64	g/cm³	ISO 1183
Density ¹¹	1.645	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.25	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.18	%	ISO 294
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.5	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.46	%	ISO 294
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.37	%	ISO 62

Table 3 of 5

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	258	°C	ASTM D648

Table 4 of 5

6 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	1345	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	170	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	15	J	ASTM D3763
Multi-Axial Impact ¹¹	4	J	ISO 6603
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	82	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	14	kJ/m²	ISO 180/1A

Table 5 of 5