LNP™ THERMOCOMP™ Compound MF0049I

Chemical Family: PolyolefinsPolypropylenes (PP)

SABIC's Specialties Business LNP™ THERMOCOMP™ Compound MF0049I is based on Polypropylene (PP) resin containing 20% glass fiber. Added features of this grade include: Flame Retardant, Impact Modified. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Sports & Recreation

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Automotive & Transportation — Transportation

Aerospace & Aviation

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polypropylene (unspecified)
Fillers Included: Glass Fiber, PTFE
Glass Fiber
PTFE
Additives Included: Flame Retardant, Impact Modifier
Flame Retardant
Impact Modifier
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 V0
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Flame Retardant
High Impact Resistance
High Modulus
High Stiffness
Impact Modified
No Added PFAS
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Aerospace Applications
Cell Phones
Computer Components
Consumer Applications
Containers
Displays
Electrical Components
Electrical Enclosure
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, 5 mm/min) ¹¹	57	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	5300	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	88	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	4700	MPa	ISO 178

Table 2 of 6

2 rows

Characteristic	Value	Unit	Method
Mold Shrinkage (flow) ᵍ ¹¹	0.34	%	SABIC method
Density ¹¹	1.37	g/cm³	ISO 1183

Table 3 of 6

3 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000032	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000118	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	156	°C	ISO 75/Af

Table 4 of 6