LNP™ THERMOCOMP™ Compound LCF62E
- Chemical Family
- Polyether Ether Ketone (PEEK)
SABIC's Specialties Business LNP™ THERMOCOMP™ LCF62E compound is based on Polyetheretherketone (PEEK) resin containing 10% carbon fiber and 30% glass fiber. Added features of this grade include: Easy Molding, Electrically Conductive.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Equipment & Parts
- Consumer Electronics
- Displays
- Industrial Automation
- Connectors
- Housings & Enclosures
- Semiconductor Manufacturing
- Switches & Relays
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyetheretherketone (PEEK)
- Fillers Included
- Carbon Fiber, Glass Fiber
- Carbon Fiber
- Glass Fiber
- Flexural Modulus
- 36490.0 - 36490.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Material Features
- Cost Effective
- ESD Protection
- Easy To Mold
- Electrically Conductive
- Good Moldability
- Good Processability
- High Stiffness
- High Strength
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Displays
- Electrical Components
- Electrical Enclosure
- Electrical Internal Frame
- Electrical/Electronic Applications
- Industrial Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 203 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 0.8 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 62980 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 296 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 17340 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 196 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 0.7 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 41090 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 391 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 36490 | MPa | ISO 178 |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.57 | — | ASTM D792 |
| Density ¹¹ | 1.57 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.02 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.09 - 2 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 3 | % | ASTM D955 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.02 | % | ISO 62 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 290 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 290 | °C | ASTM D648 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 290 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 290 | °C | ISO 75/Af |
Table 4 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 711 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 80 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 17 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 47 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
Table 5 of 5
16 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 150 | °C |
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Front - Zone 3 Temperature ⁷ | 380 - 400 | °C |
| Front - Zone 3 Temperature ⁷ | 380 - 395 | °C |
| Maximum Moisture Content ⁷ | 0.1 | % |
| Melt Temperature ⁷ | 380 - 390 | °C |
| Middle - Zone 2 Temperature ⁷ | 380 - 400 | °C |
| Middle - Zone 2 Temperature ⁷ | 365 - 375 | °C |
| Rear - Zone 1 Temperature ⁷ | 370 - 380 | °C |
| Rear - Zone 1 Temperature ⁷ | 350 - 360 | °C |