LNP™ THERMOCOMP™ Compound ZX06323

Name: LNP™ THERMOCOMP™ Compound ZX06323
Brand: LNP™ THERMOCOMP™ Compound

SABIC's Specialties Business LNP THERMOCOMP ZX06323 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing proprietary fillers. Added features of this grade include: High Dielectric Constant and Low Loss Tangent This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Density: 1950.0 - 1950.0 kg/m³
Polymer Name: PPO/PS Alloy
Flexural Modulus: 4390.0 - 4390.0 MPa
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 HB
Technology: Plastics
Labeling Claims: No Added PFAS
Fillers Included: Mineral
Titanium Dioxide
Additives Included: Heat Stabilizer
Material Features: Cost Effective
Dimensional Stability
Excellent Dielectric Properties
Heat Stabilized
High Specific Gravity
Light Weight
Low Warpage
No Added PFAS
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Automotive Interior Parts
Cell Phones
Computer Components
Consumer Applications
Containers
Displays
Electrical Components
Electrical Enclosure
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	54	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	4.2	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	4140	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	102	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	102	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	3940	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	54	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	4.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	4080	MPa	ISO 527
Flexural Modulus (at 2 mm/min) ¹¹	4390	MPa	ISO 178

Table 2 of 7

6 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.95	g/cm³	ASTM D792
Density ¹¹	1.95	g/cm³	ISO 1183
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.1	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.64	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.56	%	ASTM D955
Melt Volume Rate (at 300°C, 5.0 kg) ¹¹	8	cm³/10 min	ISO 1133

Table 3 of 7

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	122	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	122	°C	ISO 75/Af

Table 4 of 7

2 rows

Characteristic	Value	Method
Dissipation Factor (at 900 MHz) ¹¹	0.003	ASTM D150
Relative Permittivity (900MHz) ¹¹	6.4	ASTM D2520 - Mth B

Table 5 of 7

4 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	294	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	46	J/m	ASTM D256
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	20	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Table 6 of 7