LNP™ THERMOCOMP™ Compound RF006LXP

Chemical Family: Polyamides

SABIC's Specialties Business LNP THERMOCOMP RF006LXP compound is based on Nylon 6/6 resin containing 30% glass fiber. Added features of this grade include: Low Extractables. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Housewares

Building & Construction — Building Materials

Pipes & Plumbing

Printing & Packaging — Packaging

Food & Beverage Packaging
Industrial & Transport Packaging
Non-Food Consumer Packaging

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Glass Fiber
Flexural Modulus: 8820.0 - 8820.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Printing & Packaging
Technology: Plastics
Labeling Claims: Food Contact Acceptable
No Added PFAS
Material Features: Cost Effective
Food Contact Acceptable
Good Mold Release
High Modulus
High Stiffness
Low Extractables
Low Leachable
No Added PFAS
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Building Materials
Consumer Applications
Electrical Enclosure
Electrical Internal Frame
Food Packaging
Home Decors
Hoses
Household Goods
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	155	MPa	ASTM D638
Tensile Strain (Break) ¹¹	2.5	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	10300	MPa	ASTM D638
Flexural Stress ¹¹	224	MPa	ASTM D790
Flexural Modulus ¹¹	8820	MPa	ASTM D790

Table 2 of 5

3 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.41	g/cm³	ASTM D792
Density ¹¹	1.59	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.4	%	ASTM D955

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	118	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	246	°C	ASTM D648

Table 4 of 5