LNP™ THERMOCOMP™ Compound UX06028
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP THERMOCOMP UX06028 compound is based on Polyphthalamide (PPA) resin containing 40% glass fiber. Added features of this grade include: Mold Release. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Powertrain & UTH
- Consumer Electronics
- Displays
- Connectors
- Housings & Enclosures
- Semiconductor Manufacturing
- Switches & Relays
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 12000.0 - 12000.0 MPa
- Additives Included
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Good Mold Release
- High Modulus
- High Stiffness
- High Temperature Resistance
- No Added PFAS
- Very Good Heat Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Under The Hood
- Cell Phones
- Commercial Appliance
- Computer Components
- Displays
- Electrical Components
- Electrical Enclosure
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 234 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.1 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 14500 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 315 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 12000 | MPa | ISO 178 |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.14 | % | SABIC method |
| Density ¹¹ | 1.53 | g/cm³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000023 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000053 | 1/°C | ISO 11359-2 |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 55 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 13 | kJ/m² | ISO 180/1A |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 | % |
| Melt Temperature ⁷ | 315 - 330 | °C |
| Front - Zone 3 Temperature ⁷ | 325 - 340 | °C |
| Middle - Zone 2 Temperature ⁷ | 315 - 325 | °C |
| Rear - Zone 1 Temperature ⁷ | 310 - 320 | °C |
| Mold Temperature ⁷ | 140 - 165 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | 0.8 | mm | UL 94 |