LNP™ THERMOCOMP™ Compound QF0069
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP THERMOCOMP QF0069 compound is based on Nylon 6/10 resin containing 30% glass fiber. Added features of this grade include: Flame Retardant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyamide 610 (PA 610)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 9650.0 - 9650.0 MPa
- Additives Included
- Flame Retardant, Mold Release Agent
- Flame Retardant
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Flame Retardant
- Good Mold Release
- High Modulus
- High Stiffness
- Low Moisture Absorption
- No Added PFAS
- UL Listed
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Aerospace Applications
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 6
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 142 | MPa | ISO 527 |
| Tensile Stress (Yield) ¹¹ | 145 | MPa | ISO 527 |
| Tensile Stress (Yield) ¹¹ | 150 | MPa | ASTM D638 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.2 | % | ISO 527 |
| Tensile Stress (Break) ¹¹ | 145 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 150 | MPa | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8500 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 11020 | MPa | ISO 527 |
| Tensile Strain (Yield) ¹¹ | 2 | % | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 1.8 | % | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 196 | MPa | ISO 178 |
| Tensile Strain (Break) ¹¹ | 2 | % | ASTM D638 |
Table 2 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Density ¹¹ | 1.56 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.56 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.2 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.1 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.4 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.29 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.8 - 1 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.86 | % | ISO 294 |
Table 3 of 6
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000025 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000098 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 196 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 220 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 201 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000396 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00004 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000666 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000067 | 1/°C | ISO 11359-2 |
Table 4 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 45 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 37 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 603 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 64 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 9 | J | ASTM D3763 |
| Multi-Axial Impact ¹¹ | 2 | J | ISO 6603 |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.12 - 0.2 | % |
| Melt Temperature ⁷ | 270 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 280 | °C |
| Middle - Zone 2 Temperature ⁷ | 260 - 270 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 260 | °C |
| Mold Temperature ⁷ | 80 - 95 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | 1.5 | mm | UL 94 |