To catalogue
LNP™ THERMOCOMP™ Compound PFW53U
- Chemical Family
- Polyamides
LNP THERMOCOMP PFW53U compound is based on Nylon 6 resin containing 15% glass fiber, 25% wollastonite. Added features of this grade include: UV Stabilized.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Mineral, Wollastonite (CaSiO3)
- Glass Fiber
- Mineral
- Wollastonite (CaSiO3)
- Flexural Modulus
- 7290.0 - 7290.0 MPa
- Additives Included
- Light Stabilizer, Mold Release Agent
- Light Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовая инжекция.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Cost Effective
- Dimensional Stability
- Good Mold Release
- Good UV Stability
- Good Weather Stability
- High Stiffness
- Light Stabilized
- Low Warpage
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Electrical Components
- Electrical Enclosure
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 112 | MPa | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8500 | MPa | ISO 527 |
| Flexural Modulus ¹¹ | 7290 | MPa | ISO 178 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.47 | g/cm³ | ISO 1183 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 196 | °C | ISO 75/Af |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 265 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 275 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 265 - 275 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 260 | °C |
| Mold Temperature ⁷ | 80 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |