LNP™ THERMOCOMP™ Compound PF006
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP THERMOCOMP PF006 compound is based on Nylon 6 resin containing 30% glass fiber. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 6960.0 - 6960.0 MPa
- Additives Included
- Heat Stabilizer, Mold Release Agent
- Heat Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Good Mold Release
- Heat Stabilized
- High Modulus
- High Stiffness
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
20 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 160 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 165 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 128 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 129 | MPa | ASTM D638 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3.7 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.8 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.9 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 3 - 5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 9500 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8500 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8580 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 8750 | MPa | ASTM D638 |
Table 2 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.4 | % | ISO 294 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.5 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.17 - 0.5 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 1.2 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 1.2 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.9 - 1.3 | % | ISO 294 |
| Density ¹¹ | 1.37 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.37 | g/cm³ | ASTM D792 |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Mold Shrinkage (on Tensile Bar, xflow) ᵍ ¹¹ | 0.8 - 1.1 | % | SABIC method |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.86 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 6.5 | % | ISO 62-1 |
Table 3 of 7
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 203 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 70 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 85 | °C | UL 746B |
| Thermal Conductivity ¹¹ | 0.33 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000025 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000085 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 219 | °C | ASTM D648 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 206 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000305 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000306 | 1/°C | ISO 11359-2 |
Table 4 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL, PLC) ¹¹ | 0 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 1 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 5 | PLC Code | ASTM D495 |
| Volume Resistivity ¹¹ | min. 1.E+16 | Ω.cm | IEC 60093 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+16 | Ω | IEC 60093 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) ¹¹ | 3.4 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0061 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.016 | — | IEC 60250 |
Table 5 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 85 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 55 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 11 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 15 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -20°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -40°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 11 | kJ/m² | ISO 179/1eA |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 827 | J/m | ASTM D4812 |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 9 | kJ/m² | ISO 179/1eA |
| Izod Impact (Notched, at 23°C) ¹¹ | 117 | J/m | ASTM D256 |
Table 6 of 7
26 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Temperature ⁷ | 75 - 85 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Maximum Moisture Content ⁷ | 0.2 | % |
| Melt Temperature ⁷ | 250 - 280 | °C |
| Melt Temperature ⁷ | 265 - 275 | °C |
| Melt Temperature ⁷ | 255 - 265 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 280 | °C |
| Front - Zone 3 Temperature ⁷ | 275 - 290 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 260 | °C |
Table 7 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UV-light (Water exposure/immersion) ᵖ | F2 | — | UL 746C |
| UL Compliant (94HB Flame Class Rating) ᵖ | 0.75 | mm | UL 94 by SABIC-IP |
| Glow Wire Flammability Index (passes at 650°C) ʳ ᵖ | 2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) ᵖ | 25 | % | ISO 4589 |
| FMVSS Burning Speed (Thickness 2 mm) ᵖ | 6 | mm/min | FMVSS 302 |
| FMVSS Burning Speed (Thickness 3 mm) ᵖ | 2 | mm/min | FMVSS 302 |