LNP™ THERMOCOMP™ Compound PF006S
- Chemical Family
- Polyamides
LNP THERMOCOMP PF006S compound is based on Nylon 6 resin containing 30% glass fiber. Added features of this grade include: Heat Stabilized.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Industrial — Military & Defense
- Advanced Materials
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer, Mold Release Agent
- Heat Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Cost Effective
- Good Mold Release
- Heat Stabilized
- High Modulus
- High Stiffness
- Country Availability
- Canada
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 160 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 128 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 129 | MPa | ASTM D638 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3.8 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.8 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.9 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 9500 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8580 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 8750 | MPa | ASTM D638 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 230 | MPa | ISO 178 |
| Flexural Stress ¹¹ | 204 | MPa | ISO 178 |
| Flexural Stress ¹¹ | 201 | MPa | ASTM D790 |
Table 2 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.37 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.36 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.86 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.5 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.17 - 0.5 | % | ISO 294 |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 1.2 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 1.2 | % | ISO 294 |
| Water Absorption (at 23°C, saturated) ¹¹ | 6.5 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 1.53 | % | ISO 62 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 1.7 | % | ISO 62 |
Table 3 of 7
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Thermal Conductivity ¹¹ | 0.33 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000025 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000085 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 219 | °C | ASTM D648 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 206 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000305 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000306 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 215 | °C | ISO 306 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000673 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000672 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 215 | °C | ISO 306 |
Table 4 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | min. 1.E+16 | Ω.cm | IEC 60093 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+16 | Ω | IEC 60093 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) ¹¹ | 3.3 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0065 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.016 | — | IEC 60250 |
| Comparative Tracking Index ¹¹ | 500 | V | IEC 60112 |
| Comparative Tracking Index (M) ¹¹ | 375 | V | IEC 60112 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.6 | — | IEC 60250 |
Table 5 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 11 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -20°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -40°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 11 | kJ/m² | ISO 179/1eA |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 854 | J/m | ASTM D4812 |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 9 | kJ/m² | ISO 179/1eA |
| Izod Impact (Notched, at 23°C) ¹¹ | 117 | J/m | ASTM D256 |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 90 | kJ/m² | ISO 179/1eU |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 9 | J | ASTM D3763 |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 75 | kJ/m² | ISO 179/1eU |
Table 6 of 7
20 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Temperature ⁷ | 75 - 85 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Maximum Moisture Content ⁷ | 0.2 | % |
| Melt Temperature ⁷ | 250 - 280 | °C |
| Melt Temperature ⁷ | 265 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 280 | °C |
| Front - Zone 3 Temperature ⁷ | 275 - 290 | °C |
| Nozzle Temperature ⁷ | 240 - 270 | °C |
| Middle - Zone 2 Temperature ⁷ | 265 - 275 | °C |
Table 7 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glow Wire Flammability Index (passes at 650°C) | 2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 25 | % | ISO 4589 |
| FMVSS Burning Speed (Thickness 2 mm) | 6 | mm/min | FMVSS 302 |
| FMVSS Burning Speed (Thickness 3 mm) | 2 | mm/min | FMVSS 302 |