LNP™ THERMOCOMP™ Compound DF004XXC

Chemical Family: Polycarbonate (PC)

LNP THERMOCOMP DF004XXC compound is based on Polycarbonate (PC) resin containing 20% glass fiber.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: Glass Fiber
Flexural Modulus: 6100.0 - 6100.0 MPa
Additives Included: Flame Retardant, Heat Stabilizer
Flame Retardant
Heat Stabilizer
Processing Methods: Injection Molding
Note: ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 V1
UL 94 V2
Technology: Plastics
Material Features: Cost Effective
Flame Retardant
Heat Stabilized
High Modulus
High Stiffness
UL Listed
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Building Materials
Cell Phones
Computer Components
Consumer Applications
Containers
Displays
Doors
Electrical Components
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, 5 mm/min) ¹¹	121	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	3.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	6800	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	188	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	6100	MPa	ISO 178

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density ¹¹	1.36	g/cm³	ISO 1183

Table 3 of 6

4 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	143	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Table 4 of 6

2 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	65	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	12	kJ/m²	ISO 180/1A

Table 5 of 6

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.02	%
Melt Temperature ⁷	305 - 325	°C
Front - Zone 3 Temperature ⁷	320 - 330	°C
Middle - Zone 2 Temperature ⁷	310 - 320	°C
Rear - Zone 1 Temperature ⁷	295 - 305	°C
Mold Temperature ⁷	80 - 110	°C
Back Pressure ⁷	0.2 - 0.3	MPa
Screw Speed ⁷	30 - 60	rpm

Table 6 of 6