LNP™ THERMOCOMP™ Compound DC0041PQ

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP™ THERMOCOMP™ DC0041PQ compound is based on Polycarbonate (PC) resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive, Non-Brominated, Non- Chlorinated Flame Retardant, Exceptional Processing.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: Carbon Fiber, Talc
Carbon Fiber
Talc
Additives Included: Flame Retardant, Heat Stabilizer, Mold Release Agent; Flame Retardant; Heat Stabilizer; Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 V0
UL 94 V1
Technology: Plastics
Labeling Claims: Bromine-free
Chlorine-free
Material Features: Cost Effective
Electrically Conductive
Flame Retardant
Good Mold Release
Good Processability
Heat Stabilized
High Flowability
High Stiffness
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Building Materials
Cell Phones
Computer Components
Consumer Applications
Containers
Displays
Doors
Electrical Components
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	185	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.5	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	21000	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	260	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	18000	MPa	ASTM D790

Table 2 of 7

3 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.32	—	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.1	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.36	%	ASTM D955

Table 3 of 7

6 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	86	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000014	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000035	1/°C	ASTM D696
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Table 4 of 7

2 rows

Characteristic	Value	Unit	Method
Volume Resistivity ¹¹	3190000	Ω.cm	ASTM D257
Surface Resistivity ¹¹	1400000	Ω	ASTM D257

Table 5 of 7