ULTEM™ Resin AUR200G0
ULTEM™ Resin AUR200G0 is an unreinforced ULTEM recycle based grade. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Other characteristics
- Brand
- ULTEM™ Resin
- Polymer Name
- Polyether Imide (PEI)
- Flexural Modulus
- 2600.0 - 2600.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Industrial
- Printing & Packaging
- Availability
ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Recycled
- Material Features
- Amorphous
- Chemical Resistant
- Creep Resistant
- Dimensional Stability
- High Stiffness
- High Temperature Resistance
- No Added PFAS
- Unreinforced
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) | 90 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) | 5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) | 2500 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) | 120 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) | 2600 | MPa | ISO 178 |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Rate (at 360°C, 5.0 kg) | 18 | cm³/10 min | ISO 1133 |
| Density | 1.27 | g/cm³ | ISO 1183 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) | 205 | °C | ISO 75/Be |
Table 4 of 4
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | Hrs |
| Front - Zone 3 Temperature | 360 - 415 | °C |
| Hopper Temperature | 80 - 120 | °C |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 370 - 410 | °C |
| Middle - Zone 2 Temperature | 350 - 405 | °C |
| Mold Temperature | 140 - 180 | °C |
| Nozzle Temperature | 350 - 405 | °C |
| Rear - Zone 1 Temperature | 340 - 395 | °C |