ULTEM™ Resin AUR210G6
AUR210G6 is a 30% glass fiber filled grade based on ULTEM recycle. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Other characteristics
- Brand
- ULTEM™ Resin
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 6500.0 - 6500.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Availability
ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
- Key Benefits
- Heat Resistance
- Dimensional Stability
- Dielectric Performance
- Miniaturization and Thin Wall
- Resilience
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Recycled
- Material Features
- Amorphous
- Chemical Resistant
- Creep Resistant
- Dimensional Stability
- High Stiffness
- High Temperature Resistance
- No Added PFAS
- Very Good Heat Resistance
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) | 120 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) | 7500 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) | 180 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) | 6500 | MPa | ISO 178 |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (on Tensile Bar, flow) | 0.2 - 0.4 | % | SABIC method |
| Melt Volume Rate (at 337°C, 6.7 kg) | 4.5 | cm³/10 min | ISO 1133 |
| Density | 1.53 | g/cm³ | ISO 1183 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) | 212 | °C | ISO 75/Be |
Table 4 of 4
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | Hrs |
| Front - Zone 3 Temperature | 370 - 420 | °C |
| Hopper Temperature | 80 - 120 | °C |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 370 - 410 | °C |
| Middle - Zone 2 Temperature | 360 - 410 | °C |
| Mold Temperature | 140 - 180 | °C |
| Nozzle Temperature | 360 - 410 | °C |
| Rear - Zone 1 Temperature | 350 - 400 | °C |