ULTEM™ Resin AR9110

Name: ULTEM™ Resin AR9110
Brand: ULTEM™ Resin

SABIC's Specialties Business ULTEM™ Resin AR9110 is a 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: ULTEM™ Resin
Polymer Name: Polyether Imide (PEI)
Fillers Included: Glass Fiber
Additives Included: Flame Retardant
Processing Methods: Injection Molding
Markets: Automotive & Transportation
Electrical & Electronics
Industrial
Availability: ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
Technology: Plastics
Labeling Claims: Confirms to ECO-Label
Low Toxicity
No Added PFAS
Quality Standards: FAR 25.853
OSU 65/65
Material Features: Amorphous
Chemical Resistant
Dimensional Stability
Enhanced Electroplatability
Flame Retardant
Good Adhesion
Good Flow
Good Mechanical Properties

Technical data

Table 1 of 6

6 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 5 mm/min)	106	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min)	102	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min)	8	%	ASTM D638
Tensile Modulus (at 5 mm/min)	4480	MPa	ASTM D638
Flexural Stress (Yield, 2.6 mm/min, 100 mm span)	188	MPa	ASTM D790
Flexural Modulus (at 2.6 mm/min, 100 mm span)	4820	MPa	ASTM D790

Table 2 of 6

2 rows

Characteristic	Value	Unit	Method
Melt Flow Rate (at 337°C, 6.6 kgf)	12.5	g/10 min	ASTM D1238
Specific Gravity	1.4	—	ASTM D792

Table 3 of 6

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed)	207	°C	ASTM D648

Table 4 of 6