ULTEM™ Resin AUT200G4
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C).
Product families
- High Performance Thermoplastics
Other characteristics
- Brand
- ULTEM™ Resin
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 6,500.0 MPa
- Additives Included
- Flame Retardant, Mold Release Agent
- Flame Retardant
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵏ Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding. Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Printing & Packaging
- Availability
ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
- Key Benefits
- Heat Resistance
- Dimensional Stability
- Dielectric Performance
- Miniaturization and Thin Wall
- Resilience
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Low Toxicity
- Sustainable
Technical data
Table 1 of 6
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 6890 | MPa | ASTM D790 |
| Flexural Stress (Break, 2.6 mm/min, 100 mm span) ¹¹ | 227 | MPa | ASTM D790 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 6890 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 4 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 139 | MPa | ASTM D638 |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 17 | mg/1000cy | SABIC method |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 140 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 6800 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 210 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 6500 | MPa | ISO 178 |
| Ball Indentation Hardness (H358/30) ¹¹ | 150 | MPa | ISO 2039-1 |
Table 2 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 337°C, 6.6 kgf) ¹¹ | 8.4 | g/10 min | ASTM D1238 |
| Specific Gravity ¹¹ | 1.42 | — | ASTM D792 |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.3 - 0.5 | % | SABIC method |
| Density ¹¹ | 1.42 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 1 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.55 | % | ISO 62 |
| Melt Volume Rate (at 360°C, 5.0 kg) ¹¹ | 10 | cm³/10 min | ISO 1133 |
Table 3 of 6
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 210 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 211 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 212 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 225 | °C | ASTM D1525 |
| Thermal Conductivity ¹¹ | 0.28 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at -40°C to 150°C, flow) ¹¹ | 0.000021 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 150°C, xflow) ¹¹ | 0.000049 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 223 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 218 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 210 | °C | ISO 75/Be |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 205 | °C | ISO 75/Ae |
| Relative Temperature Index (Mechanical with impact) ᵏ ¹¹ | 170 | °C | UL 746B |
Table 4 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index ʳ ¹¹ | 150 | V | IEC 60112 |
| Dielectric Strength (in oil, at 0.8mm) ¹¹ | 34 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 16 | kV/mm | IEC 60243-1 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0008 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.0025 | — | IEC 60250 |
| Relative Permittivity (1 MHz) ¹¹ | 3 | — | IEC 60250 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.1 | — | IEC 60250 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | IEC 60093 |
Table 5 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 64 | J/m | ASTM D256 |
| Izod Impact (Reverse Notched, 3.2 mm) ¹¹ | 453 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 475 | J/m | ASTM D4812 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Charpy Impact (Notched, at 23°C) ¹¹ | 9 | kJ/m² | ISO 179/2C |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 35 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 35 | kJ/m² | ISO 179/1eU |
Table 6 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 370 - 410 | °C |
| Nozzle Temperature ⁷ | 360 - 410 | °C |
| Front - Zone 3 Temperature ⁷ | 370 - 420 | °C |
| Middle - Zone 2 Temperature ⁷ | 360 - 410 | °C |
| Rear - Zone 1 Temperature ⁷ | 350 - 400 | °C |
| Hopper Temperature ⁷ | 80 - 120 | °C |
| Mold Temperature ⁷ | 140 - 180 | °C |