FLEX NORYL™ Resin WCV063

Name: FLEX NORYL™ Resin WCV063
Brand: FLEX NORYL™ Resin

SABIC's Specialties Business FLEX NORYL WCV063 resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and carries UL VW-1 and UL94 V0 ratings along with a Shore D Hardness reading of 63. FLEX NORYL WCV063 resin was developed for evaluation in automotive wire + cable applications requiring ISO6722 Class A or B. It exhibits ultra thin-wall capability, Good scratch abrasion and pinch resistance, High dimensional stability, low shrinkage and warpage, Very low water absorption, chemical resistance, and good dieletrcic strength. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Product families

Applications

Automotive & Transportation — Automotive

Electrical & Electronic Systems
Powertrain & UTH
Safety Systems

Electrical & Electronics — Devices & Assemblies

Automotive Electronics

Electrical & Electronics — Parts & Components

Conduits & Cable Management

Electrical & Electronics — Wire & Cable

Jacketing & Insulation

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Other characteristics

Brand: FLEX NORYL™ Resin
Density: 1030.0 - 1030.0 kg/m³
Polymer Name: PPE/TPE Alloy
Flexural Modulus: 790.0 - 790.0 MPa
Processing Methods: Extrusion, Wire Coating Extrusion
Note: ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Electrical & Electronics
Technology: Plastics
Labeling Claims: Bromine-free
Chlorine-free
Additives Included: Flame Retardant
Heat Stabilizer
Impact Modifier
Material Features: Creep Resistant
Dimensional Stability
Ductile
Flame Retardant
Flexible
Good Processability
Heat Stabilized
High Ductility
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: RoHS Compliant
Plastics and Elastomers End Uses: Airbags
Automotive Applications
Automotive Electronics
Automotive Under The Hood
Cable Management Systems
Cables
Conduit
Electrical/Electronic Applications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion
Wire Coating Extrusion

Technical data

Table 1 of 6

12 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	28	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	28	MPa	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	90	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	840	MPa	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	720	MPa	ASTM D790
Hardness (Shore D, 10S reading) ¹¹	63	—	ASTM D2240
Tensile Stress (Yield) ¹¹	25	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	25	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	20	%	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	50	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	690	MPa	ISO 527
Flexural Modulus ¹¹	790	MPa	ISO 178

Table 2 of 6

2 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.03	—	ASTM D792
Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹	33	g/10 min	ASTM D1238

Table 3 of 6

3 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	82	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	56	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	66	°C	ISO 75/Af

Table 4 of 6