FLEX NORYL™ Resin WCP761
SABIC's Specialties Business FLEX NORYL WCP761 resin is a high flow, flexible, non-reinforced injection moldable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and carries a UL94 flame rating of V0 at 6mm. FLEX NORYL WCP761 resin is intended for evaluation in over-molding applications such as plugs, strain reliefs, and connectors. It has a Shore A Hardness reading of 78 and exhibits low specific gravity, very low water absorption, and dimensional stability.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Displays
- Conduits & Cable Management
- Connectors
- Switches & Relays
- Jacketing & Insulation
- Other Wire & Cable Applications
Product Families
- Blends & Alloys
Other characteristics
- Brand
- FLEX NORYL™ Resin
- Density
- 1050.0 - 1050.0 kg/m³
- Polymer Name
- PPE/TPE Alloy
- Processing Methods
- Extrusion, Wire Coating Extrusion
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Impact Modifier
- Mold Release Agent
- Material Features
- Creep Resistant
- Dimensional Stability
- Ductile
- Flame Retardant
- Flexible
- Good Mold Release
- Good Processability
- Heat Stabilized
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- RoHS Compliant
- UL 94
- Plastics and Elastomers End Uses
- Cable Management Systems
- Cables
- Cell Phones
- Computer Components
- Conduit
- Displays
- Electrical Components
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Wire Coating Extrusion
Technical data
Table 1 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 7 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 165 | % | ASTM D638 |
| Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹ | 50 | MPa | ASTM D790 |
| Hardness (Shore A, 30S reading) ¹¹ | 78 | — | ASTM D2240 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 8 | MPa | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 165 | % | ISO 527 |
| Flexural Modulus (at 12.5 mm/min) ¹¹ | 40 | MPa | ISO 178 |
| Tear Strength ¹¹ | 16 | N/mm | ISO 6383 |
Table 2 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.05 | — | ASTM D792 |
| Water Absorption (at 23°C, 48hrs) ¹¹ | 0.1 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.08 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.1 | % | ASTM D955 |
| Melt Flow Rate (at 210°C, 5 kgf) ¹¹ | 14.5 | g/10 min | ASTM D1238 |
| Melt Flow Rate (at 250°C, 2.16 kgf) ¹¹ | 20 | g/10 min | ASTM D1238 |
Table 3 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 1.30E+16 | Ω.cm | ASTM D257 |
| Dielectric Strength (in oil, at 2mm) ¹¹ | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) ¹¹ | 2.5 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.002 | — | IEC 60250 |
| Comparative Tracking Index ʳ ¹¹ | 600 | V | IEC 60112 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Brittleness Temperature ¹¹ | max. -40 | °C | ASTM D746 |
Table 5 of 6
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 65 - 75 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.01 | % |
| Melt Temperature ⁷ | 220 - 250 | °C |
| Nozzle Temperature ⁷ | 220 - 250 | °C |
| Front - Zone 3 Temperature ⁷ | 220 - 250 | °C |
| Middle - Zone 2 Temperature ⁷ | 210 - 240 | °C |
| Rear - Zone 1 Temperature ⁷ | 180 - 220 | °C |
| Mold Temperature ⁷ | 40 - 60 | °C |
| Back Pressure ⁷ | 3 - 10 | MPa |
| Screw Speed ⁷ | 30 - 80 | rpm |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ʳ | min. 1 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 6 | mm | UL 94 |
| Glow Wire Flammability Index (passes at 960°C) ʳ | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 775 | °C | IEC 60695-2-13 |
| Oxygen Index (LOI) ʳ | 24 | % | ISO 4589 |