FLEX NORYL™ Resin WCD795

Name: FLEX NORYL™ Resin WCD795
Brand: FLEX NORYL™ Resin

SABIC's Specialties Business FLEX NORYL™ WCD795 resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and performance capable of meeting UL 1581 VW-1 requirements. FLEX NORYL™ WCD795 resin is intended for evaluation in AC cable jacket applications that require UL62 SVE and NISPE configurations at 90C or 105C temperature rating and black color. It has a Shore A Hardness reading of 79 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Electrical & Electronics — Parts & Components

Conduits & Cable Management
Connectors
Switches & Relays

Electrical & Electronics — Wire & Cable

Jacketing & Insulation

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Other characteristics

Brand: FLEX NORYL™ Resin
Density: 1020.0 - 1020.0 kg/m³
Polymer Name: PPE/TPE Alloy
Processing Methods: Extrusion, Wire Coating Extrusion
Note: ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.. ¹⁹ Wire and cable - UL 1581 tested on 2.0mm wire with 0.12mmx20 stranded copper
Markets: Consumer Goods
Electrical & Electronics
Technology: Plastics
Labeling Claims: Bromine-free
Chlorine-free
No Added PFAS
Additives Included: Flame Retardant
Heat Stabilizer
Impact Modifier
Mold Release Agent
Material Features: Dimensional Stability
Ductile
Flame Retardant
Flexible
Good Extrusion Properties
Good Mold Release
Good Processability
Heat Stabilized
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: RoHS Compliant
Plastics and Elastomers End Uses: Cell Phones
Computer Components
Conduit
Displays
Electrical Components
Electrical/Electronic Applications
Electronic Cable Jacketing
Tablets
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion
Wire Coating Extrusion

Technical data

Table 1 of 7

7 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	14	MPa	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	240	%	ASTM D638
Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹	30	MPa	ASTM D790
Hardness (Shore A, 30S reading) ¹¹	79	—	ASTM D2240
Tensile Stress (Break, 50 mm/min) ¹¹	14	MPa	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	215	%	ISO 527
Flexural Modulus (at 12.5 mm/min) ¹¹	30	MPa	ISO 178

Table 2 of 7

2 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.02	—	ASTM D792
Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹	11	g/10 min	ASTM D1238

Table 3 of 7

6 rows

Characteristic	Value	Unit	Method
Tensile Strength (Break) ¹⁹	23	MPa	UL 1581
Tensile Elongation (Break) ¹⁹	310	%	UL 1581
Tensile Strength (Break, after 7days, at 136°C) ¹⁹	21	MPa	UL 1581
Tensile Elongation (Break, after 7days, at 136°C) ¹⁹	246	%	UL 1581
Heat Deformation (at 121°C, 250g) ¹⁹	8	%	UL 1581
VW-1 ¹⁹	Pass	—	UL 1581

Table 4 of 7

5 rows

Characteristic	Value	Unit	Method
Volume Resistivity ¹¹	1.40E+16	Ω.cm	ASTM D257
Relative Permittivity (1 MHz) ¹¹	2.6	—	ASTM D150
Dissipation Factor (at at 1 MHz) ¹¹	0.007	—	ASTM D150
Dielectric Strength (in oil, at 2mm) ¹¹	24.5	kV/mm	IEC 60243-1
Comparative Tracking Index ¹¹	600	V	IEC 60112

Table 5 of 7

1 row

Characteristic	Value	Unit	Method
Brittleness Temperature ¹¹	max. -40	°C	ASTM D746

Table 6 of 7