FLEX NORYL™ Resin WCD883CU
SABIC's Specialties Business FLEX NORYL™ WCD883CU resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This UV stabilized material contains non-halogenated flame retardant and performance capable of meeting EN 50265-2-1 requirements. FLEX NORYL™ WCD883CU resin was developed for evaluation in AC cable jacket applications such as HD 21.14 flexible cables that require EU VDE and light color. It has a Shore A Hardness reading of 88 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Displays
- Conduits & Cable Management
- Connectors
- Switches & Relays
- Jacketing & Insulation
Product Families
- Blends & Alloys
Other characteristics
- Brand
- FLEX NORYL™ Resin
- Density
- 1200.0 - 1200.0 kg/m³
- Polymer Name
- PPE/TPE Alloy
- Processing Methods
- Extrusion, Wire Coating Extrusion
- Note
¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.. ¹⁹ Wire and cable - UL 1581 tested on 2.0mm wire with 0.12mmx20 stranded copper
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Impact Modifier
- Mold Release Agent
- UV Stabilizer
- Material Features
- Dimensional Stability
- Ductile
- Flame Retardant
- Flexible
- Good Extrusion Properties
- Good Mold Release
- Good Processability
- Heat Stabilized
- Country Availability
- China (Mainland)
- Certifications and Compliance
- RoHS Compliant
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Conduit
- Displays
- Electrical Components
- Electrical/Electronic Applications
- Electronic Cable Jacketing
- Tablets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Wire Coating Extrusion
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 14 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 160 | % | ASTM D638 |
| Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹ | 65 | MPa | ASTM D790 |
| Hardness (Shore A, 30S reading) ¹¹ | 88 | — | ASTM D2240 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 12.5 | MPa | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 135 | % | ISO 527 |
| Flexural Modulus (at 12.5 mm/min) ¹¹ | 61 | MPa | ISO 178 |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 10 | g/10 min | ASTM D1238 |
Table 3 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (Break) ¹⁹ | 18 | MPa | UL 1581 |
| Tensile Elongation (Break) ¹⁹ | 260 | % | UL 1581 |
| Tensile Strength (Break, after 7days, at 80°C) ¹⁹ | 19 | MPa | UL 1581 |
| Tensile Elongation (Break, after 7days, at 80°C) ¹⁹ | 238 | % | UL 1581 |
| Heat Deformation (at 100°C, 250g) ¹⁹ | 22 | % | UL 1581 |
| Vertical Flame Test ¹⁹ | Pass | — | EN 50265-2-1 |
Table 4 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Constant (at 1.1 GHz) ¹¹ | 3 | — | SABIC method |
| Dissipation Factor (at 1.1 GHz) ¹¹ | 0.003 | — | SABIC method |
| Surface Resistivity ¹¹ | 1.70E+16 | Ω | ASTM D257 |
| Volume Resistivity ¹¹ | 1.20E+15 | Ω.cm | ASTM D257 |
| Dielectric Strength (in oil, at 2mm) ¹¹ | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index ¹¹ | 600 | V | IEC 60112 |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Brittleness Temperature ¹¹ | max. -40 | °C | ASTM D746 |
Table 6 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Oxygen Index (LOI) | 36 | % | ISO 4589 |
| Glow Wire Flammability Index (passes at 960°C) | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 3.0 mm) | 775 | °C | IEC 60695-2-13 |
Table 7 of 7
17 rows| Characteristic | Value | Unit |
|---|---|---|
| Conductor Pre-heat Temperature | 25 - 120 | °C |
| Cooling Water Air Gap | 100 - 200 | mm |
| Cross-head Temperature | 220 - 250 | °C |
| Die Temperature | 220 - 250 | °C |
| Drying Temperature | 75 - 85 | °C |
| Drying Time | 5 - 7 | Hrs |
| Drying Time (Cumulative) | 12 | Hrs |
| Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | — |
| Feed Zone Temperature | 180 - 220 | °C |
| Head Zone Temperature | 220 - 250 | °C |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 220 - 250 | °C |