LNP™ COLORCOMP™ Compound J1000Z-WH9G618

Chemical Family: Polysulfones

SABIC's Specialties Business LNP COLORCOMP J1000-WH9G618 compound is based on Polyethersulfone (PES) resin. Added features of this grade include: Extrusion, Customer Specific Color. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polyethersulfone (PES)
Flexural Modulus: 2800.0 - 2800.0 MPa
Processing Methods: Extrusion, Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Excellent Aesthetics
Good Aesthetics
Good Extrusion Properties
Good Surface Appearance
High Temperature Resistance
Unreinforced
Very Good Heat Resistance
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Interior Parts
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion
Injection Molding

Technical data

Table 1 of 5

4 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, 5 mm/min) ¹¹	85	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.6	%	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	131	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2800	MPa	ISO 178

Table 2 of 5

3 rows

Characteristic	Value	Unit	Method
Mold Shrinkage (flow) ᵍ ¹¹	0.6 - 0.8	%	SABIC method
Density ¹¹	1.38	g/cm³	ISO 1183
Water Absorption (at 23°C, 24hrs) ¹¹	0.6	%	ISO 62-1

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000058	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000062	1/°C	ISO 11359-2

Table 4 of 5