LNP™ COLORCOMP™ Compound AX98561
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
LNP™ COLORCOMP™ Compound AX98561 is based on acrylonitrile butadiene styrene (abs). This unreinforced compound features low gloss and a good balance of physical properties. It offers good processability, esthetics/visual effects, and does not contain intentionally added PFAS. Designed for injection molding, it is suitable for various sub-industries, including automotive interiors, home decoration, sport/leisure, personal accessories, home appliances, commercial appliances, electrical applications, and general industrial use.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Interior
- Equipment & Parts
- Industrial Automation
Product Families
- Styrenics
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Good Aesthetics
- Good Processability
- Low Gloss
- No Added PFAS
- Unreinforced
- Plastics and Elastomers End Uses
- Commercial Appliance
- Home Appliances
- Home Decoration
- Personal Accessories
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹ | 47.0 | MPa | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹ | 2620.0 | MPa | ASTM D638 |
| Flexural Strength (1.3 mm/min, 50 mm span) ¹ | 74.0 | MPa | ASTM D790 |
| Hardness (Rockwell R) ¹ | 112.0 | — | ASTM D785 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹ | 1.06 | — | ASTM D792 |
| Melt Flow Rate (at 230°C/3.8 kg) ¹ | 5.0 | g/10 min | ASTM D1238 |
| Melt Flow Rate (at 220°C/10.0 kgf) ¹ | 13.0 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow, 3.2 mm) ² | 0.4 - 0.6 | % | SABIC method |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ | 93.0 | °C | ASTM D648 |
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 86.0 | °C | ASTM D648 |
| Heat Deflection Temperature (1.82 MPa, 3.2mm, annealed) ¹ | 95.6 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ | 8.1e-05 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (at Rate A/120) ¹ | 107.0 | °C | ASTM D1525 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 23°C) ¹ | 220.0 | J/m | ASTM D256 |
| Izod Impact (Notched, -40°C) ¹ | 48.0 | J/m | ASTM D256 |
Table 5 of 5
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 80 - 95 | °C |
| Drying Time ³ | 2 - 4 | Hrs |
| Drying Time (Cumulative) ³ | 8.0 | Hrs |
| Maximum Moisture Content ³ | 0.1 | % |
| Melt Temperature ³ | 220 - 260 | °C |
| Nozzle Temperature ³ | 220 - 260 | °C |
| Front - Zone 3 Temperature ³ | 215 - 240 | °C |
| Middle - Zone 2 Temperature ³ | 205 - 225 | °C |
| Rear - Zone 1 Temperature ³ | 190 - 210 | °C |
| Mold Temperature ³ | 50 - 70 | °C |
| Back Pressure ³ | 0.3 - 0.7 | MPa |
| Screw Speed ³ | 30 - 60 | rpm |