NORYL™ Resin PN235
SABIC's Specialties Business NORYL PN235 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This plate able compression and injection moldable grade exhibits good impact resistance along with low moisture absorption, creep resistance, dimensional stability, and hydrolytic stability. NORYL PN235 resin is an excellent candidate for a variety of plated automotive applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Exterior & Body
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1050.0 - 1050.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Amorphous
- Dimensional Stability
- Enhanced Electroplatability
- Excellent Aesthetics
- Good Aesthetics
- Good Surface Appearance
- High Hydrolytic Stability
- Low Moisture Absorption
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 37 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 72 | % | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 55 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 1820 | MPa | ASTM D790 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.05 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.1 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Table 3 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 112 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 104 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 0°C to 100°C, flow) ¹¹ | 0.0000756 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ¹¹ | 50 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ¹¹ | 50 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ¹¹ | 50 | °C | UL 746B |
Table 4 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
| Hot Wire Ignition (PLC) ¹¹ | 3 | PLC Code | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 3 | PLC Code | UL 746A |
| High Ampere Arc Ignition (Surface, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 0 | PLC Code | UL 746A |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 347 | J/m | ASTM D256 |
| Izod Impact (Notched, at -40°C) ¹¹ | 133 | J/m | ASTM D256 |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 95 - 105 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 265 - 295 | °C |
| Nozzle Temperature ⁷ | 265 - 295 | °C |
| Front - Zone 3 Temperature ⁷ | 255 - 295 | °C |
| Middle - Zone 2 Temperature ⁷ | 245 - 290 | °C |
| Rear - Zone 1 Temperature ⁷ | 230 - 280 | °C |
| Mold Temperature ⁷ | 65 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) | 1.47 | mm | UL 94 |