NORYL™ Resin GFN2L
SABIC's Specialties Business NORYL™ GFN2L resin is a 20% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade exhibits very low moisture absorption, high strength, hydrolytic stability, Low warpage, low specific gravity, and dimensional stability. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Glazing & Window Elements
- Interior Fixtures
- Equipment & Parts
- Artificial Turf
- Consumer Electronics
- Displays
- Connectors
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1230.0 - 1230.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 5570.0 - 5570.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Stiffness
- High Hydrolytic Stability
- High Stiffness
- High Strength
- Low Moisture Absorption
- Country Availability
- China (Mainland)
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Connectors
- Construction Applications
- Displays
- Electrical/Electronic Applications
- Front Spoiler
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 98 | MPa | SABIC - Japan Method |
| Tensile Strain (Break) ¹¹ | 8 - 10 | % | SABIC - Japan Method |
| Flexural Stress ¹¹ | 142 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 5570 | MPa | ASTM D790 |
| Hardness (Rockwell R) ¹¹ | 124 | — | ASTM D785 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.23 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.06 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 11.1 | g/10 min | ASTM D1238 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 139 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.000028 - 0.000045 | 1/°C | TMA |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
Table 4 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | 1.00E+16 | Ω | ASTM D257 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.86 | — | ASTM D150 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 107 | J/m | ASTM D256 |
Table 6 of 7
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 110 - 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 300 - 325 | °C |
| Nozzle Temperature ⁷ | 300 - 325 | °C |
| Front - Zone 3 Temperature ⁷ | 290 - 325 | °C |
| Middle - Zone 2 Temperature ⁷ | 275 - 320 | °C |
| Rear - Zone 1 Temperature ⁷ | 265 - 315 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |