LEXAN™ FR Resin SLDM2005
- Chemical Family
- Polycarbonate (PC)
LEXAN SLDM2005 compound is based on Polycarbonate / Polyester blend containing proprietary fillers. Added features of this grade include: Permanently Anti-Static, Non-Halogenated Flame Retardant
Product families
Applications
- Equipment & Parts
- Industrial Automation
- Semiconductor Manufacturing
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LEXAN™ FR Resin
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- PTFE, Proprietary, Talc
- PTFE
- Proprietary
- Talc
- Flexural Modulus
- 2630.0 - 2630.0 MPa
- Additives Included
Anti-Static Agent, Flame Retardant, Heat Stabilizer, Impact Modifier, Mold Release Agent; Anti-Static Agent; Flame Retardant; Heat Stabilizer; Impact Modifier; Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.; ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V2
- Technology
- Plastics
- Material Features
- Anti-Static
- Flame Retardant
- Good Mold Release
- Heat Stabilized
- Impact Modified
- Non-Halogenated
- Non-brominated
- Non-chlorinated
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Electrical/Electronic Applications
- Industrial Applications
- Semiconductor Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 54 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 46 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 4 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 72 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2830 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 84 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2350 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 53 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 46 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 4 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 46 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2600 | MPa | ISO 527 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.25 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Melt Flow Rate (at 260°C, 2.16 kgf) ¹¹ | 17 | g/10 min | ASTM D1238 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.6 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.03 | % | ISO 62 |
Table 3 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 99 | °C | ASTM D648 |
Table 4 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ᵈ ¹¹ | 5.00E+12 | Ω | ASTM D257 |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 294 | J/m | ASTM D256 |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 90 - 100 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.04 | % |
| Melt Temperature ⁷ | 240 - 260 | °C |
| Nozzle Temperature ⁷ | 230 - 260 | °C |
| Front - Zone 3 Temperature ⁷ | 230 - 260 | °C |
| Middle - Zone 2 Temperature ⁷ | 220 - 255 | °C |
| Rear - Zone 1 Temperature ⁷ | 220 - 245 | °C |
| Mold Temperature ⁷ | 30 - 70 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-2 Flame Class Rating) ᵖ | min. 2 | mm | UL 94 |