CYCOLOY™ FR Resin CX7211
SABIC's Specialties Business CYCOLOY CX7211 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an injection moldable, medium flow, non chlorinated/brominated flame retardant grade. It has a UL94 V0@1.5mm, 5VA@2.5mm and 5VB@2.0mm flame rating. This grade has improved chemical resistance compared to standard PC/ABS blends and is a good candidate for thin wall applications.
Product families
- Blends & Alloys
Other characteristics
- Brand
- CYCOLOY™ FR Resin
- Density
- 1190.0 - 1190.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Processing Methods
- Injection Molding
- Note
ᶜ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Flame Rating
- UL 94 5VA
- UL 94 5VB
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Additives Included
- Flame Retardant
- Mold Release Agent
- Material Features
- Flame Retardant
- Good Flow
- Good Mold Release
- High Flow
- High Flowability
- High Hydrolytic Stability
- Medium Flow
- Non-brominated
- Certifications and Compliance
- UL 94
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 66 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 60 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 4 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 98 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2950 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 103 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2750 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 62 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 55 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 4 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 90 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2800 | MPa | ISO 527 |
Table 2 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.18 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᶜ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Melt Flow Rate (at 260°C, 2.16 kgf) ¹¹ | 15.5 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.19 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.24 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.12 | % | ISO 62 |
| Melt Volume Rate (at 260°C, 2.16 kg) ¹¹ | 14 | cm³/10 min | ISO 1133 |
Table 3 of 7
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 105 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 105 | °C | ISO 306 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 94 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 9.40E+01 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 89 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 102 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 96 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000075 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000551 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000075 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000614 | 1/°C | ASTM E831 |
| Thermal Conductivity ¹¹ | 0.2 | W/m-°C | ISO 8302 |
Table 4 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | min. 1.E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
| Dielectric Strength (in oil, at 0.8mm) ¹¹ | 35 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 25 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 17 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 2.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 2 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
Table 5 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 625 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 125 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 60 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 40 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 40 | kJ/m² | ISO 179/1eA |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 40 | kJ/m² | ISO 180/1A |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 10 | kJ/m² | ISO 179/1eA |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 40 | kJ/m² | ISO 179/1eA |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 90 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.04 | % |
| Melt Temperature ⁷ | 245 - 275 | °C |
| Nozzle Temperature ⁷ | 245 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 245 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 220 - 265 | °C |
| Rear - Zone 1 Temperature ⁷ | 220 - 255 | °C |
| Mold Temperature ⁷ | 60 - 80 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 7 of 7
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VA Flame Class Rating) ᵖ | min. 2.5 | mm | UL 94 |
| UL Recognized (94-5VB Flame Class Rating) ᵖ | min. 2 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 1.25 | mm | UL 94 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.5 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.25 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (at 3 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |