CYCOLOY™ FR Resin C2805
SABIC's Specialties Business CYCOLOY C2805 compound is based on Polycarbonate / Acrylonitrile Butadiene Styrene (PC/ABS) blend containing 5% PTFE. Added features of this grade include: Wear Resistant and Flame Retardant suitable for moving components in business equipment. Medium heat performance.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Electrical & Electronic Systems
- Interior
- Glazing & Window Elements
- Interior Fixtures
- Equipment & Parts
- Consumer Electronics
- Displays
- Industrial Automation
- Healthcare Packaging
- Batteries
Product Families
- Blends & Alloys
Other characteristics
- Brand
- CYCOLOY™ FR Resin
- Density
- 1220.0 - 1220.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Printing & Packaging
- Flame Rating
- UL 94 5VB
- UL 94 V0
- Technology
- Plastics
- Fillers Included
- PTFE
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Lubricant (PTFE)
- Mold Release Agent
- Material Features
- Flame Retardant
- Friction Resistant
- Good Mold Release
- Heat Stabilized
- High Impact Performance
- Non-Halogenated
- Non-brominated
- Non-chlorinated
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Building Materials
- Cell Phones
- Computer Components
- Construction Applications
- Consumer Applications
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 51 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 110 | % | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 95 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2720 | MPa | ASTM D790 |
| K-factor (xE-10, PV=2000 psi-fpm vs Steel) ¹¹ | 430 | — | SABIC method |
| Coefficient of Friction (on steel, Static) ¹¹ | 0.16 | — | ASTM D1894 |
| Coefficient of Friction (on steel, Kinetic) ¹¹ | 0.21 | — | ASTM D1894 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.22 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.4 - 0.5 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.3 - 0.5 | % | SABIC method |
Table 3 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 82 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 60 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 60 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 60 | °C | UL 746B |
Table 4 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL, PLC) ᵖ | 1 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 3) ᵖ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ᵖ | min. 1.5 | mm | UL 746A |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 133 | J/m | ASTM D256 |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 75 - 80 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.04 | % |
| Melt Temperature ⁷ | 230 - 275 | °C |
| Nozzle Temperature ⁷ | 230 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 225 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 215 - 260 | °C |
| Rear - Zone 1 Temperature ⁷ | 210 - 255 | °C |
| Mold Temperature ⁷ | 50 - 70 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VB Flame Class Rating) ᵖ | min. 2.5 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |