LNP™ COLORCOMP™ Compound DX09911
- Chemical Family
- Polycarbonate (PC)
LNP™ COLORCOMP™ Compound DX09911 is based on polycarbonate (pc) resin. This unreinforced compound features good impact resistance combined with good flow, excellent esthetics, and is colorable. It offers good processability and does not contain intentionally added PFAS. Designed for injection molding, it is suitable for various sub-industries, including automotive interiors, consumer goods, and general industrial applications.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Interior
- Equipment & Parts
Product Families
- Polycarbonates
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Flexural Modulus
- 2750.0 - 2750.0 MPa
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Consumer Goods
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Flow Properties
- Good Aesthetics
- Good Colorability
- Good Processability
- High Impact Resistance
- No Added PFAS
- Unreinforced
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹ | 62.0 | MPa | ASTM D638 |
| Tensile Stress (Yield) ¹ | 64.0 | MPa | ISO 527 |
| Tensile Stress (Break) ¹ | 56.0 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹ | 59.0 | MPa | ISO 527 |
| Tensile Strain (Yield) ¹ | 5.3 | % | ASTM D638 |
| Tensile Strain (Yield) ¹ | 5.6 | % | ISO 527 |
| Tensile Strain (Break) ¹ | 78.7 | % | ASTM D638 |
| Tensile Strain (Break) ¹ | 87.0 | % | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹ | 2060.0 | MPa | ASTM D638 |
| Flexural Modulus ¹ | 2750.0 | MPa | ASTM D790 |
| Flexural Modulus ¹ | 2300.0 | MPa | ISO 178 |
| Tensile Modulus (at 1 mm/min) ¹ | 2210.0 | MPa | ISO 527 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.2 (1.19) | g/cm³ | ASTM D792 (ISO 1183) |
| Mold Shrinkage (flow, 24 hrs) ² | 0.6 - 0.8 (0.65) | % | ASTM D955 (ISO 294) |
| Mold Shrinkage (xflow, 24 hrs) ² | 0.7 - 0.9 (0.750 | % | ASTM D955 (ISO 294) |
| Melt Flow Rate (at 300°C/6.1 kgf) ¹ | 15.0 | g/10 min | ASTM D1238 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 123.0 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 124.0 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 23°C) ¹ | 544.0 | J/m | ASTM D256 |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 13.0 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 120.0 | °C |
| Drying Time ³ | 4.0 | Hrs |
| Maximum Moisture Content ³ | 0.02 | % |
| Melt Temperature ³ | 310 - 330 | °C |
| Front - Zone 3 Temperature ³ | 310 - 330 | °C |
| Middle - Zone 2 Temperature ³ | 300 - 320 | °C |
| Rear - Zone 1 Temperature ³ | 290 - 310 | °C |
| Mold Temperature ³ | 80 - 115 | °C |
| Back Pressure ³ | 0.3 - 0.7 | MPa |
| Screw Speed ³ | 40 - 70 | rpm |