LNP™ COLORCOMP™ Compound 9X02695H

Chemical Family: Polysulfones

LNP™ COLORCOMP™ Compound 9X02695H is based on polyphenylsulfone (ppsu) and features high heat resistance and easy processing. It is characterized by high flow, healthcare/formula lock, high temperature resistance, and the absence of intentionally added PFAS. This unreinforced compound is suitable for injection molding and is used in various industries, including water management, home appliances, pharmaceutical packaging and drug delivery, surgical devices, general healthcare, patient testing, industrial packaging, and food and beverage.

Product families

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Materials

Pipes & Plumbing

Printing & Packaging — Packaging

Healthcare Packaging

Healthcare & Pharma — Pharmaceutical Manufacturing

Other Pharmaceutical Manufacturing Applications

Food & Nutrition — Processing & Packaging

Food & Beverage Manufacturing

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polyphenylsulfone (PPSU)
Flexural Modulus: 2410.0 - 2410.0 MPa
Processing Methods: Injection Molding
Note: ¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
Markets: Building & Construction
Consumer Goods
Food & Nutrition
Healthcare & Pharma
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: High Flow
No Added PFAS
Unreinforced
Very Good Heat Resistance
Plastics and Elastomers End Uses: Drug Delivery System
Food Packaging
Home Appliances
Industrial Packaging
Medical/Healthcare Applications
Pharmaceutical Packaging
Surgical Devices
Water Management
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

6 rows

Characteristic	Value	Unit	Method
Tensile Modulus (at 50 mm/min) ¹	2340.0	MPa	ASTM D638
Tensile Stress (Yield, Type I, 50 mm/min) ¹	69.6	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹	7.2	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹	90.0	%	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹	2410.0	MPa	ASTM D790
Flexural Stress (at 5% strain, 1.3 mm/min, 50 mm span) ¹	91.0	MPa	ASTM D790

Table 2 of 5

5 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹	1.29	—	ASTM D792
Water Absorption (23°C/24hrs) ¹	0.37	%	ASTM D570
Water Absorption (23°C/Saturated) ¹	1.1	%	ASTM D570
Melt Flow Rate (at 365°C/5.0 kgf) ¹	24.0	g/10 min	ASTM D1238
Mold Shrinkage (flow) ²	0.7	%	SABIC method

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹	207.0	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹	5.5e-05	1/°C	ASTM D696

Table 4 of 5

1 row

Characteristic	Value	Unit	Method
Izod Impact (Notched, 23°C) ¹	690.0	J/m	ASTM D256