ULTEM™ Resin DT1810EVUCL

Name: ULTEM™ Resin DT1810EVUCL
Brand: ULTEM™ Resin

ULTEM™ Resin DT1810EVUCL has improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility.

Product families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: ULTEM™ Resin
Polymer Name: Polyether Imide (PEI)
Flexural Modulus: 3100.0 - 3100.0 MPa
Additives Included: Flame Retardant, Heat Stabilizer, Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Translucent
Transparent
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Healthcare & Pharma
Industrial
Printing & Packaging
Availability: ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
Technology: Plastics
Labeling Claims: Low Toxicity

Technical data

Table 1 of 5

14 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	103	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	85	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	7	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	80	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	3210	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	145	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	3320	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	98	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	80	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	7	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	80	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2500	MPa	ISO 527

Table 2 of 5

7 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.28	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Melt Flow Rate (at 337°C, 6.6 kgf) ¹¹	43	g/10 min	ASTM D1238
Density ¹¹	1.28	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	0.36	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.08	%	ISO 62
Melt Volume Rate (at 360°C, 5.0 kg) ¹¹	56	cm³/10 min	ISO 1133

Table 3 of 5

10 rows

Characteristic	Value	Unit	Method
Vicat Softening Temperature (Rate B/50) ¹¹	192	°C	ASTM D1525
Vicat Softening Temperature (Rate B/50) ¹¹	192	°C	ISO 306
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	173	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	178	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 150°C, flow) ¹¹	0.00006	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 150°C, xflow) ¹¹	0.00006	1/°C	ASTM E831
Coefficient of Thermal Expansion (at 23°C to 150°C, flow) ¹¹	0.000055	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 150°C, xflow) ¹¹	0.000055	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	195	°C	ISO 306
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120104, sp=100mm) ¹¹	168	°C	ISO 75/Ae

Table 4 of 5

8 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	No break	J/m	ASTM D4812
Izod Impact (Unnotched, at -30°C) ¹¹	No break	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	32	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	35	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	48	J	ASTM D3763
Izod Impact (Notched, 80104, at 23°C) ¹¹	2	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -30°C) ¹¹	2	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	2	kJ/m²	ISO 179/1eA

Table 5 of 5