To catalogue
ULTEM™ Resin DU319
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
SABIC's Specialties Business Transparent Polyetherimide blend with PET resin. Material is RoHS compliant and is also US FDA and EU Food Contact Compliant in recognized colors. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- ULTEM™ Resin
- Polymer Name
- Polyether Imide (PEI)
- Processing Methods
- Injection Molding
- Color
- Translucent
- Transparent
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Printing & Packaging
- Availability
ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
- Key Benefits
- Heat Resistance
- Dimensional Stability
- Dielectric Performance
- Miniaturization and Thin Wall
- Resilience
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Food Contact Acceptable
- No Added PFAS
- Sustainable
Technical data
Table 1 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) | 110 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) | 82 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) | 7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) | 60 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) | 3370 | MPa | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) | 165 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) | 110 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) | 75 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) | 6 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) | 36 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) | 3300 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) | 155 | MPa | ISO 178 |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 3.2 mm) | 0.6 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 295°C, 6.6 kgf) | 8.1 | g/10 min | ASTM D1238 |
| Water Absorption (at 23°C, saturated) | 0.5 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) | 0.17 | % | ISO 62 |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Specific Gravity | 1.29 | — | ASTM D792 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) | 181 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) | 177 | °C | ISO 306 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) | 165 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) | 0.0000486 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) | 0.0000486 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (Rate B/120) | 180 | °C | ISO 306 |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Instrumented Dart Impact Total Energy (at 23°C) | 40 | J | ASTM D3763 |
| Izod Impact (Notched, at 23°C) | 26 | J/m | ASTM D256 |
| Izod Impact (Reverse Notched, 3.2 mm) | 950 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*4, at 23°C) | 4 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) | 4 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) | 3 | kJ/m² | ISO 179/1eA |
Table 5 of 5
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure | 0.7 - 1.4 | MPa |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 - 8 | Hrs |
| Drying Time (Cumulative) | 24 | Hrs |
| Front - Zone 3 Temperature | 295 - 325 | °C |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 300 - 330 | °C |
| Middle - Zone 2 Temperature | 290 - 320 | °C |
| Mold Temperature | 95 - 150 | °C |
| Nozzle Temperature | 300 - 330 | °C |
| Rear - Zone 1 Temperature | 280 - 315 | °C |
| Screw Speed | 50 - 100 | rpm |