LNP™ STAT-KON™ Compound DEL32P

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP™ STAT-KON™ DEL32P compound is based on Polycarbonate (PC) resin containing 10% carbon fiber,15% PTFE. Added features of this grade include: Internally Lubricated, Electrically Conductive, Wear Resistant, Exceptional Processing.

Product families

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ STAT-KON™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: Carbon Fiber, PTFE
Carbon Fiber
PTFE
Additives Included: Lubricant (PTFE), Lubricant (Unspecified), Mold Release Agent; Lubricant (PTFE); Lubricant (Unspecified); Mold Release Agent
Processing Methods: Injection Molding
Note: ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Electrical & Electronics
Industrial
Technology: Plastics
Material Features: ESD Protection
Electrically Conductive
Friction Resistant
Good Mold Release
Good Processability
High Flowability
High Stiffness
High Strength
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Computer Components
Electrical/Electronic Applications
Industrial Applications
Semiconductor Applications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 4

2 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.32	g/cm³	ASTM D792
Melt Volume Rate (at 300°C, 3.8 kg) ¹¹	19	cm³/10 min	ISO 1133

Table 2 of 4

1 row

Characteristic	Value	Unit	Method
Surface Resistivity ᵈ ¹¹	100 - 1000000	Ω	ASTM D257