LNP™ ELCRIN™ 610001UiQ2
SABIC's Specialties Business LNP ELCRIN 610001UiQ2 (also known as ELCRIN ER011568) is a non-brominated, non-chlorinated flame retardant Polycarbonate / Polybutylene Terephthalate (PC/PBT) alloy, utilizing iQ PBT generation 2 technology with minimum 12% post consumer recycled content. Added features of this material include: good impact strength, good chemical resistance, improved heat resistance, bright white color achievable, UL V-0 rating at 1.5 mm thickness and easy flow ability.
Other characteristics
- Brand
- LNP™ ELCRIN
- Density
- 1250.0 - 1250.0 kg/m³
- Polymer Name
- PC/PBT Alloy
- Labeling Claims
Bromine-free, Chlorine-free, Contains PCR Resin, Recyclable, Recycled, Sustainable; Bromine-free; Chlorine-free; Contains PCR Resin; Recyclable; Recycled; Sustainable
- Melt Flow Index
- 23.0 - 23.0 g/10 min
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Additives Included
- Flame Retardant
- Heat Stabilizer
- UV Stabilizer
- Material Features
- Chemical Resistant
- Ductile
- Flame Retardant
- Good Aesthetics
- Good Colorability
- Good Flow
- Good Mechanical Properties
- Good Moldability
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
Technical data
Table 1 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.25 | — | ASTM D792 |
| Melt Flow Rate (at 265°C, 5.0 kgf) ¹¹ | 23 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 265°C, 5.0 kg) ¹¹ | 20 | cm³/10 min | ISO 1133 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.06 | % | ISO 62-4 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.11 | % | ISO 62-1 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.6 - 0.8 | % | SABIC method |
| Mold Shrinkage (xflow) ᵍ ¹¹ | 0.6 - 0.8 | % | SABIC method |
Table 2 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 55 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 54 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 120 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2170 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 85 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2260 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 55 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 46 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 105 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2120 | MPa | ISO 527 |
Table 3 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 85 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 105 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 114 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 115 | °C | ASTM D1525 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000071 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000076 | 1/°C | ASTM E831 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 90 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 105 | °C | ISO 75/Bf |
Table 4 of 6
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 800 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 342 | J/m | ASTM D256 |
| Izod Impact (Notched, at 0°C) ¹¹ | 700 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 60 | J | ASTM D3763 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 50 | J | ASTM D3763 |
| Instrumented Dart Impact Peak Force (at 23°C) ¹¹ | 4500 | N | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 58 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 17 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 0°C) ¹¹ | 44 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 60 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 18 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 0°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 48 | kJ/m² | ISO 179/1eA |
Table 5 of 6
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 90 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.04 | % |
| Melt Temperature ⁷ | 245 - 275 | °C |
| Nozzle Temperature ⁷ | 245 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 245 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 220 - 265 | °C |
| Rear - Zone 1 Temperature ⁷ | 220 - 255 | °C |
| Mold Temperature ⁷ | 60 - 80 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 6 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.4 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 0.8 | mm | UL 94 |