NORYL™ Resin NCF1010
SABIC's Specialties Business NORYL™ NCF1010 is a compound based on PPE+PS resin containing 10% Glass Fiber, 10% Carbon Fiber and 10% PTFE. Added features: Structural and Wear Resistant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Chassis & Brake
- Glazing & Window Elements
- Interior Fixtures
- Consumer Electronics
- Displays
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1210.0 - 1210.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 7610.0 - 7610.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Fillers Included
- Carbon Fiber
- Glass Fiber
- PTFE
- Material Features
- Friction Resistant
- High Stiffness
- High Strength
- Wear Resistant
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Bearings
- Building Materials
- Cash Dispenser (ATM)
- Cell Phones
- Chassis
- Commercial Appliance
- Computer Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 97 | MPa | SABIC - Japan Method |
| Tensile Strain (Break) ¹¹ | 7 - 7 | % | SABIC - Japan Method |
| Flexural Stress ¹¹ | 129 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 7610 | MPa | ASTM D790 |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.21 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.06 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.3 - 0.6 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.5 - 0.8 | % | ASTM D955 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 134 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.000025 - 0.000045 | 1/°C | TMA |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 58 | J/m | ASTM D256 |
Table 5 of 6
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 300 - 305 | °C |
| Front - Zone 3 Temperature ⁷ | 300 - 310 | °C |
| Middle - Zone 2 Temperature ⁷ | 290 - 300 | °C |
| Rear - Zone 1 Temperature ⁷ | 275 - 290 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |