NORYL™ Resin NC212
NORYL™ Resin NC212
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1160.0 - 1160.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 6080.0 - 6080.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V1
- Technology
- Plastics
- Fillers Included
- Carbon Fiber
- Additives Included
- Flame Retardant
- Material Features
- ESD Protection
- Electrically Conductive
- Flame Retardant
- Good Moldability
- Good Processability
- High Flowability
- High Stiffness
- High Strength
- Country Availability
- China (Mainland)
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Cash Dispenser (ATM)
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Displays
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 83 | MPa | SABIC - Japan Method |
| Tensile Strain (Break) ¹¹ | 4 - 6 | % | SABIC - Japan Method |
| Flexural Stress ¹¹ | 125 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 6080 | MPa | ASTM D790 |
| Hardness (Rockwell M) ¹¹ | 88 | — | ASTM D785 |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.16 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.06 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 134 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.000025 - 0.000045 | 1/°C | TMA |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity | 1000 - 100000000 | Ω | ASTM D257 |
Table 5 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 49 | J/m | ASTM D256 |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |