NORYL™ Resin N1050
SABIC's Specialties Business NORYL™ N1050 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade was designed for improved dimensional stability and flow. This grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 2.5mm and V0 at 1.5mm along with impact strength, very low moisture absorption, excellent dimensional stability, and good electrical properties. NORYL™ N1050 resin is an excellent candidate for a variety of applications requiring electrically insulating properties, low moisture absorption and low warpage.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Electrical & Electronic Systems
- Glazing & Window Elements
- Interior Fixtures
- Automotive Electronics
- Consumer Electronics
- Displays
- Batteries
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1100.0 - 1100.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2530.0 - 2530.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 5VA
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Additives Included
- Flame Retardant
- Material Features
- Amorphous
- Dimensional Stability
- Excellent Aesthetics
- Flame Retardant
- Good Aesthetics
- Good Surface Appearance
- High Hydrolytic Stability
- Low Moisture Absorption
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- AC Charging Cabinet
- Appliances
- Automotive Electronics
- Automotive Under The Hood
- Batteries
- Battery Cell
- Battery Pack
- Building Materials
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 63 | MPa | SABIC - Japan Method |
| Tensile Strain (Break) ¹¹ | 40 | % | SABIC - Japan Method |
| Flexural Stress ¹¹ | 98 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 2530 | MPa | ASTM D790 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 17 | g/10 min | ASTM D1238 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 105 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.00007 | 1/°C | TMA |
Table 4 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | 1.00E+16 | Ω | ASTM D257 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.78 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.003 | — | ASTM D150 |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 117 | J/m | ASTM D256 |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 75 - 80 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 250 - 275 | °C |
| Nozzle Temperature ⁷ | 250 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 240 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 225 - 270 | °C |
| Rear - Zone 1 Temperature ⁷ | 215 - 265 | °C |
| Mold Temperature ⁷ | 55 - 75 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) | 1.5 | mm | UL 94 |
| UL Recognized (94-5VA Flame Class Rating) | 2.5 | mm | UL 94 |