NORYL™ Resin V0150B
SABIC's Specialties Business NORYL V0150B resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm along with a UL746C Outdoor Suitability rating of F1. exhibits good low temperature impact resistance, damp heat performance, low moisture absorption and good dimensional stability. NORYL V0150B resin is an excellent candidate for parts that are exposed to tough outdoor environments, such as Solar / Photovoltaic (PV) junction boxes and outdoor housings and enclosures. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1110.0 - 1110.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2400.0 - 2400.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 5VA
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Impact Modifier
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Heat Stabilized
- High Hydrolytic Stability
- Impact Modified
- Low Moisture Absorption
- Low Shrinkage
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Connectors
- Construction Applications
- Displays
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 70 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 60 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 7 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2500 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 105 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2550 | MPa | ASTM D790 |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 35 | mg/1000cy | SABIC method |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 70 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 55 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 4 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 10 | % | ISO 527 |
Table 2 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.11 | — | ASTM D792 |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 3.5 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.11 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.18 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.06 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 5.0 kg) ¹¹ | 10 | cm³/10 min | ISO 1133 |
Table 3 of 7
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 145 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 155 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 135 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000075 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000075 | 1/°C | ASTM E831 |
| Thermal Conductivity ¹¹ | 0.27 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.00009 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (approximate maximum) ¹¹ | 140 | °C | IEC 60695-10-2 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 160 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 155 | °C | ISO 306 |
Table 4 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
| Dielectric Strength (in oil, at 0.8mm) ¹¹ | 33 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0009 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.003 | — | IEC 60250 |
| Comparative Tracking Index ʳ ¹¹ | 250 | V | IEC 60112 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.8 | — | IEC 60250 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 0.8 | mm | UL 746A |
Table 5 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 330 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 180 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 50 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 13 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 14 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 5 | kJ/m² | ISO 179/1eA |
Table 6 of 7
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 110 - 120 | °C |
| Drying Time ⁷ | 2 - 3 | Hrs |
| Melt Temperature ⁷ | 300 - 320 | °C |
| Nozzle Temperature ⁷ | 280 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 300 - 320 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 300 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Hopper Temperature ⁷ | 80 - 100 | °C |
| Mold Temperature ⁷ | 100 - 130 | °C |
Table 7 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VA Flame Class Rating) ʳ | min. 2 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 1 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 0.8 | mm | UL 94 |
| Glow Wire Flammability Index (at 1 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ʳ | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ʳ | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ʳ | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 775 | °C | IEC 60695-2-13 |
| UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |