NORYL™ Resin ENG265
SABIC's Specialties Business NORYL™ ENG265 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This material is suitable for profile extrusion and exhibits very good hydrolytic stability, low moisture absorption, good dimensional stability. NORYL™ ENG265 resin is an excellent candidate for a variety of profile extrusion applications. *See ENG265F resin for NSF 61 certification. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Glazing & Window Elements
- Interior Fixtures
- Connectors
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1060.0 - 1060.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Processing Methods
- Extrusion
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Additives Included
- Heat Stabilizer
- Material Features
- Amorphous
- Dimensional Stability
- Good Extrusion Properties
- Heat Stabilized
- High Hydrolytic Stability
- Low Moisture Absorption
- Low Shrinkage
- Low Specific Gravity
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Building Materials
- Construction Applications
- Electrical Components
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 7
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 50 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 50 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 56 | MPa | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 3.3 | % | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 3.1 | % | ISO 527 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 28 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2400 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 89 | MPa | ASTM D790 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 88 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2550 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2450 | MPa | ASTM D790 |
| Hardness (Rockwell R) ¹¹ | 119 | — | ASTM D785 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.06 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.06 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 8.5 | g/10 min | ASTM D1238 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 8 | cm³/10 min | ISO 1133 |
Table 3 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 132 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 118 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 126 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.0000594 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 137 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 141 | °C | ISO 306 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 90 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 105 | °C | UL 746B |
Table 4 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 19.7 | kV/mm | ASTM D149 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.65 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0004 | — | ASTM D150 |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 4) ¹¹ | min. 6 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 4) ¹¹ | min. 6 | mm | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 7 | PLC Code | ASTM D495 |
Table 5 of 7
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Adapter Temperature | 250 | °C |
| Barrel - Zone 1 Temperature | 205 | °C |
| Barrel - Zone 2 Temperature | 205 | °C |
| Barrel - Zone 3 Temperature | 225 | °C |
| Barrel - Zone 4 Temperature | 225 | °C |
| Die Temperature | 250 | °C |
| Drying Temperature | 105 - 115 | °C |
| Drying Time | 2 - 4 | Hrs |
| Drying Time (Cumulative) | 8 | Hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 225 - 255 | °C |
Table 6 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 186 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 114 | J/m | ASTM D256 |
| Color (at -30°C) ¹¹ | 25 | J | ASTM D3029 |
| Color (at -40°C) ¹¹ | 5 | J | ASTM D3029 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 39 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 13 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Charpy Impact (Notched, at 23°C) ¹¹ | 13 | kJ/m² | ISO 179/2C |
| Charpy Impact (Notched, at -30°C) ¹¹ | 10 | kJ/m² | ISO 179/2C |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |