NORYL™ Resin NHP8000VT3
SABIC’s NORYL NHP8000VT3 resin delivers thin-wall, non-brominated, non-chlorinated flame retardance and achieves one of the highest comparative tracking index level (CTI PLC0). Potential applications include insulation film for higher-voltage EV batteries. This resin is a non-reinforced blend of polyphenylene ether (PPE) and polystyrene (PS)that can provide outstanding heat resistance, ultra-thin-wall flame retardancy, and superior tracking resistance performance. NORYL NHP8000VT3 Resin may be evaluated in extrusion and injection molding processes. It contains a non-brominated and non-chlorinated flame retardant, ensuring adherence to many safety standards while avoiding specific halogens. NORYL NHP8000VT3 Resin has: - A Comparative Tracking Index (CTI) of PLC 0 (600V) - A UL94 flame rating of V0 at 0.25mm thickness It leverages an extraordinary technology that provides: - High impact strength - Heat resistance - Dimensional stability - Hydrolytic stability - Electrical performance - Low moisture absorption - Low specific gravity. SABIC’s NORYL NHP8000VT3 resin won a bronze 2023 Edison Award in the Enhanced Performance category.
Product families
Applications
- Electrical & Electronic Systems
- Automotive Electronics
- Batteries
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1100.0 - 1100.0 kg/m³
- Polymer Name
- PPE/PS Alloy
- Flexural Modulus
- 2600.0 - 2600.0 MPa
- Processing Methods
- Extrusion, Injection Molding, Thermoforming
- Note
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ³ Extrusion parameters are only mentioned as general guidelines.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Impact Modifier
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Electrical Properties
- Good Processability
- Good Tracking Resistance
- Heat Stabilized
- High Hydrolytic Stability
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Electronics
- Battery Pack
- Busbar
- Busbar Insulation Layer
- Diaphragms
- EV Battery
- EV Battery Pack
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
- Thermoforming
Technical data
Table 1 of 8
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 66.8 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 4.2 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 10.8 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2491 | MPa | ASTM D638 |
| Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 108 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2600 | MPa | ASTM D790 |
Table 2 of 8
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.1 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.04 | % | ISO 62-1 |
| Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 11.7 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow) ¹¹ | 0.73 | % | SABIC method |
| Mold Shrinkage (xflow) ¹¹ | 0.79 | % | SABIC method |
Table 3 of 8
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 150 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 133 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 166 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 155 | °C | ASTM D1525 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Ball Pressure Test (approximate maximum) ¹¹ | 140 | °C | IEC 60695-10-2 |
Table 4 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | 7.50E+16 | Ω | ASTM D257 |
| Volume Resistivity ¹¹ | 6.20E+15 | Ω.cm | ASTM D257 |
| Comparative Tracking Index (UL, PLC) ᵖ ¹¹ | 0 | PLC Code | UL 746A |
Table 5 of 8
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 1.10E+02 | °C |
| Drying Time ³ | 3 - 4 | Hrs |
| Barrel - Zone 1 Temperature ³ | 210 | °C |
| Barrel - Zone 2 Temperature ³ | 275 | °C |
| Barrel - Zone 3 Temperature ³ | 280 | °C |
| Barrel - Zone 4 Temperature ³ | 280 | °C |
| Die Temperature ³ | 285 | °C |
| Roll Stack Temperature - Bottom ³ | 20 - 30 | °C |
| Roll Stack Temperature - Middle ³ | 120 - 130 | °C |
| Roll Stack Temperature - Top ³ | 120 - 140 | °C |
Table 6 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 211 | J/m | ASTM D256 |
| Izod Impact (Notched, at -40°C) ¹¹ | 84 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | No break | J/m | ASTM D4812 |
| Izod Impact (Unnotched, at -40°C) ¹¹ | 1830 | J/m | ASTM D4812 |
Table 7 of 8
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 100 - 120 | °C |
| Drying Time ⁷ | 3 - 5 | Hrs |
| Melt Temperature ⁷ | 280 - 330 | °C |
| Nozzle Temperature ⁷ | 250 - 330 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 330 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 330 | °C |
| Rear - Zone 1 Temperature ⁷ | 280 - 330 | °C |
| Mold Temperature ⁷ | 70 - 120 | °C |
| Back Pressure ⁷ | 0.3 - 0.8 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 8 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 0.25 | mm | UL 94 |