LNP™ ELCRIN™ FXE8543RCC
- Chemical Family
- Polycarbonate (PC)Siloxanes
LNP™ ELCRIN™ FXE8543RCC is based on polycarbonate (pc) siloxane copolymer resin with 40% post-consumer recycled (pcr) content. This grade features medium flow and is colorable, designed for applications requiring enhanced esthetics and a wider color spectrum compared to traditional PCR grades. It offers VISUALFX capability in "Illuminate" and "Edge Glow" colors, catering to diverse application needs.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Off Road & Recreational Vehicle (RV)
Product Families
- Polycarbonates
Other characteristics
- Brand
- LNP™ ELCRIN
- Polymer Name
- Polycarbonate-Siloxane Copolymer
- Flexural Modulus
- 2280.0 - 2280.0 MPa
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. ³ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ⁴ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Contains PCR Resin
- No Added PFAS
- Material Features
- Good Aesthetics
- Good Colorability
- Medium Flow
- No Added PFAS
- Unreinforced
- Plastics and Elastomers End Uses
- Audio Equipment
- Building Materials
- Computer Components
- Computer Data Storage
- Electronic Data Processing
- Heavy Vehicles
- Home Appliances
- Personal Accessories
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) ¹ | 58.0 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹ | 62.0 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹ | 6.2 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹ | 132.0 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 2130.0 | MPa | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹ | 2280.0 | MPa | ISO 178 |
| Flexural Strength (2 mm/min) ¹ | 91.0 | MPa | ISO 178 |
| Tensile Modulus (at 50 mm/min) ¹ | 2070.0 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹ | 58.0 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹ | 63.0 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹ | 6.4 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹ | 130.0 | % | ASTM D638 |
Table 2 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.23 | g/cm³ | ISO 1183 |
| Water Absorption (23°C/24hrs) ¹ | 0.15 | % | ISO 62-1 |
| Water Absorption (23°C/24hrs) ¹ | 0.14 | % | ASTM D570 |
| Melt Volume Rate (at 300°C/1.2 kg) ¹ | 16.0 | cm³/10 min | ISO 1133 |
| Specific Gravity ¹ | 1.19 | — | ASTM D792 |
| Melt Flow Rate (at 300°C/1.2 kgf) ¹ | 17.0 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow) ³ | 0.4 - 0.8 | % | SABIC method |
| Mold Shrinkage (xflow) ³ | 0.4 - 0.8 | % | SABIC method |
Table 3 of 6
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 124.0 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 138.0 | °C | ISO 75/Bf |
| Vicat Softening Temperature (at Rate B/50) ¹ | 142.0 | °C | ISO 306 |
| Vicat Softening Temperature (at Rate B/50) ¹ | 142.0 | °C | ASTM D1525 |
| Vicat Softening Temperature (at Rate B/120) ¹ | 144.0 | °C | ISO 306 |
| Vicat Softening Temperature (at Rate B/120) ¹ | 144.0 | °C | ASTM D1525 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹ | 6.6e-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹ | 7.2e-05 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 126.0 | °C | ASTM D648 |
| Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ | 139.0 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 23°C to 50°C, flow) ¹ | 6.6e-05 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 23°C to 50°C, xflow) ¹ | 7.2e-05 | 1/°C | ASTM E831 |
Table 4 of 6
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 52.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched 80*10*4 0°C) ¹ | 20.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched 80*10*4 -30°C) ¹ | 16.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 237.0 | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹ | 59.0 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 0°C, V-notch Edgew 80*10*4 sp=62mm) ¹ | 23.0 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹ | 18.0 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹ | 330.0 | kJ/m² | ISO 179/1eU |
| Izod Impact (Notched, 23°C) ¹ | 770.0 | J/m | ASTM D256 |
| Izod Impact (Notched, 0°C) ¹ | 600.0 | J/m | ASTM D256 |
| Izod Impact (Notched, -30°C) ¹ | 190.0 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 23°C) ¹ | 2700.0 | J/m | ASTM D4812 |
Table 5 of 6
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁴ | 120.0 | °C |
| Drying Time ⁴ | 3 - 4 | Hrs |
| Maximum Moisture Content ⁴ | 0.02 | % |
| Melt Temperature ⁴ | 295 - 315 | °C |
| Rear - Zone 1 Temperature ⁴ | 270 - 295 | °C |
| Middle - Zone 2 Temperature ⁴ | 280 - 305 | °C |
| Front - Zone 3 Temperature ⁴ | 295 - 315 | °C |
| Nozzle Temperature ⁴ | 290 - 310 | °C |
| Mold Temperature ⁴ | 70 - 95 | °C |
| Back Pressure ⁴ | 0.3 - 0.7 | MPa |
| Screw Speed ⁴ | 40 - 70 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized 94HB Flame Class Rating ² | 0.47 | mm | UL 94 |