LNP™ ELCRIN™ DMX1234RCC
- Chemical Family
- Polycarbonate (PC)
LNP™ ELCRIN™ DMX1234RCC is an improved scratch-resistant polycarbonate copolymer containing 25% post-consumer recycled content. This standard flow, UV-stabilized, custom-colorable resin is unreinforced and features excellent scratch resistance, impact resistance, and weatherability with no PFAS intentionally added. Suitable for injection molding, it is ideal for a variety of applications, including automotive interiors, sport/leisure, personal accessories, home and commercial appliances, electrical devices and displays, and electrical components and infrastructure.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
- Interior
Electrical & Electronics — Devices & Assemblies
- Displays
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- LNP™ ELCRIN
- Polymer Name
- Polycarbonate (PC) Copolymer
- Flexural Modulus
- 2503.0 - 2503.0 MPa
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² ;Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Good Scratch Resistance
- Good Weather Stability
- Impact Resistance
- No Added PFAS
- UV Stabilized
- Unreinforced
- Plastics and Elastomers End Uses
- Commercial Appliance
- Electrical Components
- Electrical Devices
- Electronic Displays
- Home Appliances
- Personal Accessories
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) ¹ | 77.0 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹ | 61.0 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹ | 7.0 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹ | 92.0 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 2474.0 | MPa | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹ | 2503.0 | MPa | ISO 178 |
| Flexural Stress (Yield, 2 mm/min) ¹ | 108.0 | MPa | ISO 178 |
| Tensile Modulus (at 50 mm/min) ¹ | 2630.0 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹ | 80.0 | % | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹ | 8.0 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹ | 63.0 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹ | 78.0 | MPa | ASTM D638 |
Table 2 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.18 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C/50% RH/24 hrs) ¹ | 0.04 | % | ASTM D570 |
| Water Absorption (23°C/24hrs) ¹ | 0.09 | % | ASTM D570 |
| Specific Gravity ¹ | 1.18 | — | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ¹ | 0.5 - 0.8 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ¹ | 0.5 - 0.8 | % | ASTM D955 |
| Melt Volume Rate (at 300°C/1.2 kg) ¹ | 14.0 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 300°C/1.2 kg) ¹ | 14.0 | cm³/10 min | ASTM D1238 |
| Melt Flow Rate (at 300°C/1.2 kgf) ¹ | 16.0 | g/10 min | ASTM D1238 |
Table 3 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 118.0 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 132.0 | °C | ISO 75/Bf |
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 120.0 | °C | ASTM D648 |
| Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ | 133.0 | °C | ASTM D648 |
| Vicat Softening Temperature (at Rate B/50) ¹ | 138.0 | °C | ISO 306 |
| Vicat Softening Temperature (at Rate B/50) ¹ | 138.0 | °C | ASTM D1525 |
| Vicat Softening Temperature (at Rate B/120) ¹ | 140.0 | °C | ISO 306 |
| Vicat Softening Temperature (at Rate B/120) ¹ | 140.0 | °C | ASTM D1525 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ | 6.8e-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ | 6.8e-05 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ | 7.0e-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ | 7.0e-05 | 1/°C | ASTM E831 |
Table 4 of 5
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched 80*10*3 +23°C) ¹ | 3.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched 80*10*3 -30°C) ¹ | 20.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched 80*10*3 +23°C) ¹ | 169.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched 80*10*3 -30°C )¹ | 87.0 | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹ | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹ | 1.0 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹ | 324.0 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹ | 93.0 | kJ/m² | ISO 179/1eU |
| Izod Impact (Notched, 23°C) ¹ | 30.0 | J/m | ASTM D256 |
| Izod Impact (Notched, 0°C) ¹ | 32.0 | J/m | ASTM D256 |
| Izod Impact (Notched, -30°C) ¹ | 31.0 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 23°C) ¹ | NB | J/m | ASTM D4812 |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ² | 120.0 | °C |
| Drying Time ² | 3 - 4 | Hrs |
| Maximum Moisture Content ² | 0.02 | % |
| Melt Temperature ² | 295 - 315 | °C |
| Rear - Zone 1 Temperature ² | 260 - 280 | °C |
| Middle - Zone 2 Temperature ² | 280 - 305 | °C |
| Front - Zone 3 Temperature ² | 295 - 315 | °C |
| Nozzle Temperature ² | 290 - 310 | °C |
| Mold Temperature ² | 70 - 95 | °C |