LNP™ ELCRIN™ W10001iQ
- Chemical Family
- Polyesters
SABIC's Specialties Business LNP ELCRIN W10001iQ compound is based on Polybutylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 44% Post-Consumer Recycling (PCR) weight content. Added features of this grade include: Non-Chlorinated, Non-Brominated Flame Retardant, Excellent Chemical Resistance and UL94V0 Flame Rating. This is a good candidate for a variety of applications needing a more sustainable FR and PBT solution.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Terminal Blocks Plugs & Sockets
Product Families
- Recycled Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- LNP™ ELCRIN
- Density
- 1310.0 - 1310.0 kg/m³
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Labeling Claims
Bromine-free, Chlorine-free, Contains PCR Resin, Recyclable, Recycled, Sustainable; Bromine-free; Chlorine-free; Contains PCR Resin; Recyclable; Recycled; Sustainable
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 5VA
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Material Features
- Chemical Resistant
- Flame Retardant
- Non-brominated
- Non-chlorinated
- Recyclable
- Unreinforced
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
- Value Proposition Compared to Fossil Based PBT Compounds
Reduced carbon, energy footprint; Improved social impact; Similar mechanical properties & color space; Drop-in solution for existing tools; REACH, RoHS and EPEAT compliant; SABIC LNP Health care policy compliance. May comply with regional food contact regulations .
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 41 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 10 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2740 | MPa | ASTM D638 |
| Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 66 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2430 | MPa | ASTM D790 |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 250°C, 2.16 kg) ¹¹ | 20 | cm³/10 min | ISO 1133 |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 1.8 - 2.8 | % | SABIC method |
Table 3 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 55 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 150 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 208 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate A/120) ¹¹ | 207 | °C | ASTM D1525 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 75 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 75 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 75 | °C | UL 746B |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 550 | J/m | ASTM D4812 |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 100 - 120 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 245 - 260 | °C |
| Nozzle Temperature ⁷ | 230 - 255 | °C |
| Front - Zone 3 Temperature ⁷ | 240 - 260 | °C |
| Middle - Zone 2 Temperature ⁷ | 235 - 250 | °C |
| Rear - Zone 1 Temperature ⁷ | 230 - 240 | °C |
| Hopper Temperature ⁷ | 40 - 60 | °C |
| Mold Temperature ⁷ | 40 - 100 | °C |
Table 6 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-1 Flame Class Rating) ᵖ | 0.8 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1 | mm | UL 94 |
| UL Recognized (94-5VA Flame Class Rating) ᵖ | min. 3 | mm | UL 94 |