LNP™ ELCRIN™ 610009UXiQ

SABIC's Specialties Business LNP ELCRIN 610009UXiQ compound is based on Polycarbonate / Polybutylene Terephthalate (PC/PBT) blend, utilizing ELCRIN iQ upcycling technology containing minimum 19% Post-Consumer Recycling (PCR) weight content. Added features of this grade include: Flame Retardant, UL746C F1 Rating, UL94 V0 and 5VA Flame Rating, UV Resistant, Impact Modified, Excellent Chemical Resistance. This is a good candidate for applications in the electrical industry including bobbins, switches, and enclosures.

Other characteristics

Brand: LNP™ ELCRIN
Density: 1340.0 - 1340.0 kg/m³
Polymer Name: PC/PBT Alloy
Labeling Claims: Contains PCR Resin, Recyclable, Recycled, Sustainable; Contains PCR Resin; Recyclable; Recycled; Sustainable
Melt Flow Index: 9.3 - 9.3 g/10 min
Processing Methods: Extrusion, Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Industrial
Personal Care
Printing & Packaging
Flame Rating: UL 746C F1
UL 94 5VA
UL 94 HB
UL 94 V0
Technology: Plastics
Additives Included: Flame Retardant
Impact Modifier
UV Stabilizer
Material Features: Chemical Resistant
Flame Retardant
Good UV Stability
Good Weather Stability
High Impact Resistance
Impact Modified
Non-chlorinated
Recyclable
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Interior Parts
Bobbins
Cash Dispenser (ATM)
Cell Phones
Commercial Appliance
Computer Components
Plastics and Elastomers Functions: Resin

Technical data

Table 1 of 7

14 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	48	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	41	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	4.9	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	74	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	2000	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	75	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2100	MPa	ASTM D790
Tensile Stress (Yield, 50 mm/min) ¹¹	48	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	40	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	4.6	%	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	74.8	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2190	MPa	ISO 527

Table 2 of 7

7 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.35	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	1.1 - 1.4	%	SABIC method
Melt Flow Rate (at 250°C, 5 kgf) ¹¹	9.3	g/10 min	ASTM D1238
Density ¹¹	1.34	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	0.08	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.08	%	ISO 62
Melt Volume Rate (at 250°C, 5 kg) ¹¹	7	cm³/10 min	ISO 1133

Table 3 of 7

10 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	95	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	127	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000816	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000816	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000974	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000974	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	122	°C	ISO 75/Bf
Relative Temperature Index (Electrical) ᵖ ¹¹	120	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	120	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	140	°C	UL 746B

Table 4 of 7

8 rows

Characteristic	Value	Unit	Method
Comparative Tracking Index (UL, PLC) ᵖ	2	PLC Code	UL 746A
Arc Resistance (Tungsten, PLC) ᵖ	6	PLC Code	ASTM D495
High Voltage Arc Track Rate (PLC) ᵖ	4	PLC Code	UL 746A
Hot Wire Ignition (PLC 2) ᵖ	min. 3	mm	UL 746A
Hot Wire Ignition (PLC 3) ᵖ	min. 0.63	mm	UL 746A
Hot Wire Ignition (PLC 4) ᵖ	min. 0.46	mm	UL 746A
High Ampere Arc Ignition (PLC 3) ᵖ	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 4) ᵖ	min. 0.46	mm	UL 746A

Table 5 of 7

6 rows

Characteristic	Value	Unit	Method
Izod Impact (Notched, at 23°C) ¹¹	490	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	167	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	50	J	ASTM D3763
Izod Impact (Notched, 80104, at 23°C) ¹¹	31	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -30°C) ¹¹	10	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	34	kJ/m²	ISO 179/1eA

Table 6 of 7