LNP™ LUBRICOMP™ Compound RFL26S
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP LUBRICOMP RFL26S compound is based on Nylon 6/6 resin containing 30% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 9300.0 - 9300.0 MPa
- Additives Included
- Heat Stabilizer, Lubricant (PTFE)
- Heat Stabilizer
- Lubricant (PTFE)
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Friction Resistant
- Heat Stabilized
- High Stiffness
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 185 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 3.3 | % | ASTM D638 |
| Flexural Stress ¹¹ | 275 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 9300 | MPa | ASTM D790 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.43 | g/cm³ | ASTM D792 |
| Wear Factor Washer ¹¹ | 5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.66 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.57 | — | ASTM D3702 Modified: Manual |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 253 | °C | ASTM D648 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1121 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 128 | J/m | ASTM D256 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 265 - 275 | °C |
| Mold Temperature ⁷ | 95 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |