NORYL GTX™ Resin GTX944
SABIC's Specialties Business NORYL GTX944 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance along with improved processability and increased impact performance. NORYL GTX944 resin may be an excellent candidate for Firefighter Helmet applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Electrical & Electronic Systems
- Glazing & Window Elements
- Interior Fixtures
- Batteries
- Connectors
- Housings & Enclosures
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL GTX™ Resin
- Density
- 1070.0 - 1070.0 kg/m³
- Polymer Name
- PPO/Nylon Alloy
- Flexural Modulus
- 1900.0 - 1900.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Additives Included
- Heat Stabilizer
- Impact Modifier
- Mold Release Agent
- Material Features
- Chemical Resistant
- Dimensional Stability
- Good Mold Release
- Heat Stabilized
- High Hydrolytic Stability
- High Impact Resistance
- High Stiffness
- High Tensile Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Agricultural Applications
- Back Panel
- Battery Cover
- Building Materials
- Connectors
- Construction Applications
- Corner Support Plates
- Crash Protection
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 50 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 45 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 100 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 1900 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 75 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 1950 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 50 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 45 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 3.5 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 50 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2000 | MPa | ISO 527 |
Table 2 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.08 | — | ASTM D792 |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 1.4 - 1.8 | % | SABIC method |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 1.4 - 1.7 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 1.1 - 1.4 | % | SABIC method |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 12.5 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.07 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 3.5 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 1.2 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 12 | cm³/10 min | ISO 1133 |
Table 3 of 7
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 180 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 180 | °C | ISO 306 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 185 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00009 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0001 | 1/°C | ASTM E831 |
| Thermal Conductivity ¹¹ | 0.24 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00009 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00009 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 240 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 185 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 175 | °C | ISO 75/Be |
Table 4 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 2.20E+13 | Ω.cm | IEC 60093 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.072 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.024 | — | IEC 60250 |
| Comparative Tracking Index ¹¹ | 600 | V | IEC 60112 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.5 | — | IEC 60250 |
Table 5 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 680 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 280 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 55 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 55 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -20°C) ¹¹ | 25 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 25 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 55 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 25 | kJ/m² | ISO 179/1eA |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 100 - 120 | °C |
| Drying Time ⁷ | 2 - 3 | Hrs |
| Maximum Moisture Content ⁷ | 0.07 | % |
| Melt Temperature ⁷ | 290 - 320 | °C |
| Nozzle Temperature ⁷ | 280 - 310 | °C |
| Front - Zone 3 Temperature ⁷ | 290 - 320 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 300 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 80 - 120 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Compliant (94HB Flame Class Rating) ¹¹ | 1.6 | mm | UL 94 by SABIC-IP |
| Oxygen Index (LOI) ¹¹ | 21 | % | ISO 4589 |