NORYL GTX™ Resin GTX810
SABIC's Specialties Business NORYL GTX810 resin is a 10% glass fiber reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 3000 MPa), excellent chemical resistance, and high heat resistance. NORYL GTX810 resin is an excellent candidate for a wide variety of applications including automotive under the hood, electrical and lighting components, security (CCTV) housings. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Automotive Lighting
- Electrical & Electronic Systems
- Powertrain & UTH
- Interior Fixtures
- Automotive Electronics
- Consumer Electronics
- Displays
- Lighting
- Batteries
- Connectors
- Housings & Enclosures
- Sensors & Actuators
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL GTX™ Resin
- Density
- 1160.0 - 1160.0 kg/m³
- Polymer Name
- PPO/Nylon Alloy
- Flexural Modulus
- 3900.0 - 3900.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Impact Modifier
- Material Features
- Chemical Resistant
- Dimensional Stability
- Heat Stabilized
- High Hydrolytic Stability
- High Stiffness
- High Strength
- High Tensile Strength
- Impact Modified
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Electronics
- Automotive Under The Hood
- Back Panel
- Battery Cover
- Cell Phones
- Computer Components
- Connectors
- Corner Support Plates
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
25 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.18 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.16 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.162 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.5 | % | ASTM D570 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.19 | % | ISO 62-4 |
| Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹ | 0.56 | % | ISO 62-4 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.77 | % | ISO 62-1 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.77 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 2.12 | % | ISO 62-1 |
| Water Absorption (at 23°C, saturated) ¹¹ | 2.12 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 3.3 | % | ISO 62-1 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 11 | cm³/10 min | ISO 1133 |
Table 2 of 7
29 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 1 mm/min) ¹¹ | 3200 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 4200 | MPa | ISO 527 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 65 | MPa | ISO 527 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 102 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 96 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 89 | MPa | ASTM D638 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 65 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 95 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 88 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 91 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 10 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 5.5 | % | ASTM D638 |
Table 3 of 7
24 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 241 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 192 | °C | ISO 75/Af |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 250 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 240 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 200 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 221 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 221 | °C | ASTM D1525 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00006 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000044 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000044 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000087 | 1/°C | ISO 11359-2 |
Table 4 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| High Voltage Arc Track Rate (PLC) ¹¹ | 3 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
Table 5 of 7
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 80 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 53 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 85 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 40 | kJ/m² | ISO 180/1U |
| Charpy Impact (Notched, at 23°C) ¹¹ | 6 | kJ/m² | ISO 179/2C |
| Charpy Impact (Notched, at -20°C) ¹¹ | 4 | kJ/m² | ISO 179/2C |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 60 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 40 | kJ/m² | ISO 179/1eU |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6.8 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 6.5 | kJ/m² | ISO 179/1eA |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 740 | J/m | ASTM D4812 |
Table 6 of 7
24 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 100 - 110 | °C |
| Drying Temperature ⁷ | 95 - 105 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time ⁷ | 2 - 3 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.07 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Melt Temperature ⁷ | 280 - 300 | °C |
| Minimum Moisture Content ⁷ | 0.02 | % |
| Nozzle Temperature ⁷ | 280 - 305 | °C |
| Nozzle Temperature ⁷ | 270 - 290 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 300 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| Oxygen Index (LOI) ʳ | 26 | % | ISO 4589 |