NORYL GTX™ Resin GTX679
SABIC's Specialties Business NORYL GTX679 resin is a conductive, mineral reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized to allow for primer-less electrostatic painting. NORYL GTX679 resin has improved impact / elongation, and the mineral content allows for the material to be used in structural applications such as metal and thermoset resin replacement. This material is available only in black. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Sports & Recreation
- Electrical & Electronic Systems
- Exterior & Body
- Interior
- Batteries
- Housings & Enclosures
- Off Road & Recreational Vehicle (RV)
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL GTX™ Resin
- Density
- 1240.0 - 1240.0 kg/m³
- Polymer Name
- PPO/Nylon Alloy
- Flexural Modulus
- 4440.0 - 4440.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Fillers Included
- Mineral
- Additives Included
- Conductive Agent
- Impact Modifier
- Mold Release Agent
- Material Features
- Chemical Resistant
- Conductive
- Dimensional Stability
- Electrically Conductive
- Excellent Aesthetics
- Good Aesthetics
- Good Mold Release
- Good Stiffness
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Back Panel
- Battery Cover
- Corner Support Plates
- Crash Protection
- Front Panel
- Recreational Vehicle Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 64 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 3 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 4 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 4450 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 108 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 4000 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 61 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 61 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 4.79E+03 | MPa | ISO 527 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.24 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.7 - 0.9 | % | SABIC method |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 16 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.24 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 3.6 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.7 | % | ISO 62 |
| Melt Volume Rate (at 220°C, 5.0 kg) ¹¹ | 14 | cm³/10 min | ISO 1133 |
Table 3 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 185 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 185 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 185 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000595 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000595 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000649 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000649 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 188 | °C | ISO 306 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 184 | °C | ISO 75/Bf |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 39 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 31 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 7 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 3 | kJ/m² | ISO 179/1eA |
Table 5 of 5
15 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 95 - 105 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.07 | % |
| Minimum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 275 - 300 | °C |
| Nozzle Temperature ⁷ | 275 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 300 | °C |
| Middle - Zone 2 Temperature ⁷ | 265 - 300 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 300 | °C |
| Mold Temperature ⁷ | 65 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 1.4 | MPa |