NORYL PPX™ Resin PPX7200U
SABIC's Specialties Business NORYL PPX7200U resin is a non-reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This UV-stabilized, injection moldable grade exhibits improved chemical resistance and surface esthetics along with high-temperature performance, excellent melt strength, modulus, impact resistance, hydrolytic and dimensional stability. NORYL PPX7200U resin is an excellent candidate for applications such as hot water tank components and outdoor housings and enclosures. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Pipes & Plumbing
- Artificial Turf
- Consumer Electronics
- Displays
- Connectors
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL PPX™ Resin
- Density
- 990.0 - 990.0 kg/m³
- Polymer Name
- PPE/PP Alloy
- Flexural Modulus
- 1600.0 - 1600.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Additives Included
- Heat Stabilizer
- Impact Modifier
- UV Stabilizer
- Material Features
- Chemical Resistant
- Dimensional Stability
- Heat Stabilized
- High Hydrolytic Stability
- High Impact Resistance
- High Stiffness
- High Tensile Strength
- Impact Modified
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Displays
- Electrical Components
- Electrical/Electronic Applications
- Enclosure
- Faucet System Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 34 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 33 | MPa | ASTM D638 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 28 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 27 | MPa | ASTM D638 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 8.2 | % | ISO 527 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 10 | % | ASTM D638 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 115 | % | ISO 527 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 130 | % | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 1670 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 1240 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 48 | MPa | ASTM D790 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 48 | MPa | ISO 178 |
Table 2 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.6 - 0.8 | % | SABIC method |
| Density ¹¹ | 0.99 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 260°C, 5.0 kg) ¹¹ | 18 | cm³/10 min | ISO 1133 |
| Specific Gravity ¹¹ | 0.99 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.6 - 0.8 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.6 - 0.8 | % | SABIC method |
| Melt Flow Rate (at 260°C, 5.0 kgf) ¹¹ | 16 | g/10 min | ASTM D1238 |
Table 3 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.0001 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00014 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 146 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 103 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 107 | °C | ISO 306 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 110 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 71 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000099 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000108 | 1/°C | ASTM E831 |
Table 4 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 14 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 12 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 6 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 80 | kJ/m² | ISO 179/1eU |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1441 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 149 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 36 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
Table 5 of 6
17 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 60 - 65 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 260 - 290 | °C |
| Nozzle Temperature ⁷ | 260 - 290 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 240 - 280 | °C |
| Middle - Zone 2 Temperature ⁷ | 240 - 285 | °C |
| Rear - Zone 1 Temperature ⁷ | 225 - 275 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 30 - 50 | °C |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |