NORYL™ Resin NP6100
SABIC's Specialties Business NORYL NP6100 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) designed for high heat resistance with good strength, toughness and robust FR performance. This extrudable grade contains non-brominated, non-chlorinated flame retardant. NORYL NP6100 resin may be an excellent candidate for mining pipe applications as well as low smoke cable channel applications where EN45545 R22 certificate ( European railway standard for small electrical parts) is required. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Exterior & Body
- Interior
- Pipes & Plumbing
- Circuit Breakers
- Conduits & Cable Management
- Rail & Mass Transit
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1080.0 - 1080.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2350.0 - 2350.0 MPa
- Processing Methods
- Extrusion
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Benefits
- Good ductility at low temperatures
- Good extrudability
- Low density: 1.1g/cm3
- High stiffness: 2.3 GPa
- Low smoke density: ISO 5659-2
- BPT 125°C
- R22 HL3 according to EN 45545
- Flame Rating
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Overview
NORYL™ NP6100 resin combines excellent thermal resistance, ductility and processability. Developed to help to address stringent requirements For low smoke density and low smoke corrosion, NORYL™ NP6100 offers a unique balance of mechanical properties and flame resistance. The flame retardants used in NORYL™ resin are bromine- and chlorine-free.
- Additives Included
- Flame Retardant
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Extrusion Properties
- High Hydrolytic Stability
- High Temperature Resistance
- Low Moisture Absorption
- Low Shrinkage
- Country Availability
- China (Mainland)
- Certifications and Compliance
- UL 94
- Typical Industry
Material requirements for cable channels include:; GWFI 960°C; Low smoke density, low corrosivity; BPT>75°C; Low weight; Good impact resistance over a wide temperature range
- Plastics and Elastomers End Uses
- Automotive Applications
- Conduit
- Electrical/Electronic Applications
- Miniature Circuit Breakers
- Pipes
- Rails
- Relay Bases
- Switches
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 47 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 4.5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 10.5 | % | ASTM D638 |
| Flexural Stress (Yield, at 6.4 mm) ¹¹ | 95 | MPa | ASTM D790 |
| Flexural Modulus (at 6.4 mm) ¹¹ | 2200 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 68 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 52 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 4.5 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 7 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2330 | MPa | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2350 | MPa | ISO 178 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 77 | MPa | ISO 178 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.08 | — | ASTM D792 |
| Melt Flow Rate (at 280°C, 10.0 kgf) ¹¹ | 10.5 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Volume Rate (at 280°C, 10.0 kg) ¹¹ | 11 | cm³/10 min | ISO 1133 |
Table 3 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 121 | °C | ASTM D648 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 146 | °C | ISO 75/Bf |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 151 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 153 | °C | ISO 306 |
Table 4 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Adapter Temperature | 255 - 275 | °C |
| Die Temperature | 255 - 275 | °C |
Table 5 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 510 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 180 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 39.9 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 15.8 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 37 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 21 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
Table 6 of 7
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 90 - 100 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 255 - 275 | °C |
| Rear - Zone 1 Temperature ⁷ | 235 - 255 | °C |
| Middle - Zone 2 Temperature ⁷ | 255 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 255 - 275 | °C |
| Nozzle Temperature ⁷ | 255 - 275 | °C |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Compliant (94V-1 Flame Class Rating) | 1.5 | mm | UL 94 by SABIC-IP |
| Glow Wire Flammability Index (passes at 960°C) | 1 | mm | IEC 60695-2-12 |
| Smoke Density (DS-max, 25 kW/m², 1.5 mm) | 47 | — | ISO 5659-2 |